Ceramic Steel Putty

HIGH TEMPERATURE CERAMIC - METALLIC PASTES
Technical Bulletin A3
Pyro-Putty High Temperature Ceramic-Metallic Putties are used to seal joints and repair
defects in cast aluminum, cast iron, steel and stainless steel. Formulated using the most
advanced organic and inorganic-ceramic resin technologies, these advanced materials resist
temperatures to 2000 F. Applications for Pyro-Putty are widespread and found typically in the
aerospace, automotive, foundry, heat treating, incineration and power generation industries.
PRODUCT HIGHLIGHTS
TYPICAL APPLICATIONS
Afterburners
Boilers
Castings
Exhaust Stacks
Flanges
Furnaces
Headers
Incinerators
Manifolds
Molds and Dies
Ovens
Heat Exchangers
Pumps
Blowers
Piping
Ducting
Turbines
Resists Temperatures to 2000 F
Resurfaces and Repairs Defects

Pyro-Putty 653 seals Babcock & Wilcox furnace door.
Reduces Scrap
Machinable
Gets Stronger with Heat
Readily Painted or Powder Coated
Easy and Safe to Use
Pyro-Putty
653
Ceramic and Stainless-Filled, One-Part, Water-Based Paste.
For Vertical Surfaces and Applications to 1/2 Thick.
Repairs Cast Iron, Steel and Stainless Parts to 2000 F.
Pyro-Putty 950
Ceramic Fiber-Filled, Organic Caulk.
For Sealing High Temperature Flanges, Joints to 950 F, 750 psi.
Cures Into a Tough, Pliable, Inert Material.
Pyro-Putty 1000
Ceramic and Aluminum-Filled, Two-Part, Water-Based Paste.
For Applications to 1/2 Thick.
Repairs Cast Aluminum Parts to 1400 F.
Pyro-Putty 1500
Ceramic-Filled, One-Part, Thixotropic Paste.
Used Primarily to Seal Boiler Doors and Molten Metal Systems.
Easy to Apply and Removable; For uses to 2300 F.
Pyro-Putty 2400
Ceramic and Stainless-Filled, One-Part, Water-Based Paste.
Repairs Cast Iron, Steel and Stainless Parts to 2000 F.
Pyro-Putty 2500
Ceramic and Black Iron Oxide-filled One-Part, Water-Based Paste.
Repairs Cast Iron, and Steel Parts to 1600 F.
Pyro-Putty 2400 repairs flanges on a F & J gas engine.
Pyro-Putty 950 seals high temperature flange.
Pyro-Putty 2400 repairs exhaust pipe leak.
PYRO-PUTTY PROPERTIES
Product
Type
653
950
1000
1500
2400
2500
Inorganic
Organic
Inorganic
Inorganic
Inorganic
Inorganic
Filler
Stainless Ceramic Fiber Aluminum
Maximum Temp., F (C) 2000 (1093) 950 (510)
1400 (760)
Specific Gravity, gms/cc
1.9
1.09
1.8
Viscosity, cps
No. Components
Curing
Mix Ratio, powder:liquid

Air Set, hours
Heat Cure, F, hrs
Color
Shelf Life, mos.
Storage, F
Packaging
Ceramic
Stainless
2300 (1260) 2000 (1093)
1.27
1.50
Iron Oxide
1600 (871)
2.90
Paste
Paste
Paste
Paste
Paste
Paste
1
N/A
N/A
2:1
N/A
N/A
N/A
2-4
N/A
2-4
1-2
2-4
2-4
200, 3
400,1 or 225, 6
160, 1-2
200, 1
200, 2-4
200, 3
Gray
Silver Gray
Light Gray
Gray-Brown
Dark Gray
Black
40-90
40-90
40-90
40-90
40-90
40-90
Pt, Qt, Gal, 5 Gal 11 oz Cartridge Pt, Qt, Gal, 5 Gal
AREMCO PRODUCTS, INC.
Pt, Qt, Gal, 5 Gal,

Pt, Qt, Gal, 5 Gal Pt, Qt, Gal, 5 Gal
11 oz Cartridge
Pyro-Putty 1000 repairs cast aluminum manifold.
P.O. Box 517, 707-B Executive Boulevard, Valley Cottage, NY 10989

(845) 268-0039 FAX: (845) 268-0041 E-mail: [email protected] Website: www.aremco.com
Rev. 1/08
11
APPLICATION PROCEDURES
Mixing
Pyro-Putty 1000:
1) A heat cure is not required for cross-sections less than 1/8
thick. Air dry at room temperature for a minimum of 2-4 hours
prior to use.
2) A heat cure is recommended for cross-sections greater than
1/8 thick Air dry at room temperature for a minimum of 2-4
hours, then heat cure at 160 F for 1-2 hours.
3) After curing, this product can be sanded to achieve a bright
aluminum appearance.
All products should be mixed thoroughly to a uniform consistency

prior to use. Product viscosities may be reduced by adding a
maximum of 5-10% by weight of the appropriate thinner. Thinner
may be ordered by adding a -T to the product number (eg. 653-T).
Pyro-Putty 1500:
1) This product dries at room temperature and cures in service
at the operating temperature of the equipment.
Surface Preparation
A
3
All surfaces must be free of oil, grease, dirt, corrosives or other

contaminants before application. Porous metal castings should
be baked at high temperature to burn off embedded oils. Smooth
metal surfaces should be abrasive blasted with a coarse media
to a minimum SP-10 near white blast (0.001 minimum profile) for
best results.
The mix ratio for Pyro-Putty 1000 is 2.0 parts powder to 1.0-1.5 parts
liquid. This ratio will produce the consistency of a thick paste. PyroPutty 1000 will outgas slightly after mixing and it is recommended
that the mixture be limited to the amount required for a specific
application. Store mixed material at room temperature in a plastic
container that is approximately twice the mixture volume. Allow to
outgas for 24 hours. Remix contents thoroughly prior to use. Note that
mixture will not begin to harden in a closed container for over 24 hours.
Hardening will initiate when mixture is removed from container and
exposed to air.
Application
Pyro-Putty products may be applied using a spatula, putty knife
or caulk gun. For cross-sections greater than 1/8 - 1/4 multiple
applications should be made to avoid blistering. Cross-sections
for all products should not exceed 1/2 - 3/4 (3/8 maximum for
Pyro-Putty 2400).
Pyro-Putty 2400:
1) Air dry at room temperature for a minimum of 5-7 hours,
longer for thick cross-sections.
2) A heat cure is not required if the use temperature exceeds
400 F. Otherwise, heat cure at 200 F for 3 hours.
Pyro-Putty 2500:
1) Air dry at room temperature for a minimum of 1 hour, longer
for thick cross-sections.
2) Heat cure at 200 F for 2 hours or air dry at room temperature
for 16 hours prior to use.
Storage
Curing
Unopened containers have a six month shelf life when stored at

room temperature. Make sure opened containers are capped
securely to prevent evaporation. Place a plastic film in between
the cap and container to prevent air leakage. The container may
be inverted periodically to minimize settling. Store container
between 40 F and 90 F.
The following instructions are guidelines for curing. Alternative cure

times may be appropriate depending on the size of the application.
Safety
Pyro-Putty 653:
1) Air dry for 2 hours at room temperature and up to 4 hours for
thick cross-sections.
2) Heat cure at 200 F for 3 hours.
3) For multiple applications, air set for 1-2 hours between coats,
then heat cure at 200 F for 3-4 hours after the last coat.
Read Material Safety Data Sheet carefully before using any of

the above products. Prolonged skin contact should be avoided
due to possible irritation. In the uncured state, materials can be
washed from the skin with a mild soap and water. If any material
contacts eyes, flush continuously with water or neutralizing
solutions, then consult a physician immediately.
Pyro-Putty 950:
1) This product can be cured in service at the operating
temperature of the equipment.
2) For curing before service, heat cure the joint without pressure
at 400 F for 30-60 minutes or 225 F for 4-6 hours.
Refer to Price List for complete order information.

Aremco Products makes no warranty express or implied concerning the use of this product.
The user assumes all risk of use or handling whether or not in accordance with directions or suggestions, or used singly or in combination with other products.
12

Ceramic Steel Putty

Uploaded by

Copyright:

Available Formats

Ceramic Steel Putty

Uploaded by

Document Information

Original Description:

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Ceramic Steel Putty

Uploaded by

Copyright:

Available Formats

HIGH TEMPERATURE CERAMIC - METALLIC PASTES

Resists Temperatures to 2000 F

Resurfaces and Repairs Defects

Pyro-Putty 2400 repairs flanges on a F & J gas engine.

Pyro-Putty 950 seals high temperature flange.

Pyro-Putty 2400 repairs exhaust pipe leak.

Mix Ratio, powder:liquid

Pt, Qt, Gal, 5 Gal 11 oz Cartridge Pt, Qt, Gal, 5 Gal

AREMCO PRODUCTS, INC.

Pt, Qt, Gal, 5 Gal,

Pyro-Putty 1000 repairs cast aluminum manifold.

P.O. Box 517, 707-B Executive Boulevard, Valley Cottage, NY 10989

All products should be mixed thoroughly to a uniform consistency

All surfaces must be free of oil, grease, dirt, corrosives or other

Unopened containers have a six month shelf life when stored at

The following instructions are guidelines for curing. Alternative cure

Read Material Safety Data Sheet carefully before using any of

Refer to Price List for complete order information.

You might also like