    Zinc Anode 304 MZS is a two-part inorganic zinc silicate coating recommended for protecting steel structures against corrosion in coastal and industrial environments. It provides excellent cathodic protection through a tough, abrasion-resistant film. The coating dries within 30 minutes and can withstand temperatures up to 400°C continuously or 426°C intermittently. It has good resistance to chemicals, salts, and weathering. The product has a pot life of 6-8 hours and requires surface preparation of Sa 2.5 before application by conventional or airless spray.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    DS 164 02 ZincAnode304 MZS

    Uploaded by

    Power Power
    129 views2 pages
    Zinc Anode 304 MZS is a two-part inorganic zinc silicate coating recommended for protecting steel structures against corrosion in coastal and industrial environments. It provides excellent cathodic protection through a tough, abrasion-resistant film. The coating dries within 30 minutes and can withstand temperatures up to 400°C continuously or 426°C intermittently. It has good resistance to chemicals, salts, and weathering. The product has a pot life of 6-8 hours and requires surface preparation of Sa 2.5 before application by conventional or airless spray.

    Original Description:

    ZincAnode304 MZS

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Zinc Anode 304 MZS is a two-part inorganic zinc silicate coating recommended for protecting steel structures against corrosion in coastal and industrial environments. It provides excellent cathodic protection through a tough, abrasion-resistant film. The coating dries within 30 minutes and can withstand temperatures up to 400°C continuously or 426°C intermittently. It has good resistance to chemicals, salts, and weathering. The product has a pot life of 6-8 hours and requires surface preparation of Sa 2.5 before application by conventional or airless spray.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    129 views2 pages

    DS 164 02 ZincAnode304 MZS

    Uploaded by

    Power Power
    Zinc Anode 304 MZS is a two-part inorganic zinc silicate coating recommended for protecting steel structures against corrosion in coastal and industrial environments. It provides excellent cathodic protection through a tough, abrasion-resistant film. The coating dries within 30 minutes and can withstand temperatures up to 400°C continuously or 426°C intermittently. It has good resistance to chemicals, salts, and weathering. The product has a pot life of 6-8 hours and requires surface preparation of Sa 2.5 before application by conventional or airless spray.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    Zinc Anode 304 MZS Inorganic Zinc Silicate Coating

    USES
    Recommended for use on steel structurals, exterior of storage tanks, bulk handling equipment, pipelines, etc. The product is suitable for both coastal and industrial/inland environments.

    SCOPE
    A two pack solvent base inorganic zinc primer for protection of steel against severe corrosive environment . It provides outstanding cathodic protection and forms a tough abrasion resistant film. It is however, not recommended for contacts with strong acids or alkalis of pH below 5 or exceeding 10. The coating attains water resistance within 30 minutes of application and is unaffected by rain, condensation or dew.

    PRODUCT DATA
    Type : Two pack pack, self cured Composition : Ethyl Silicate/Metallic Zinc Mixing Ratio : Part A: Part B; 17.6 ltr: 2.4 ltr Pot Life : 6-8 hours Application : Conventional or Airless spray Recommended DFT : 60-75 microns per coat Corresponding WFT : 100-125 microns per coat Theoretical Spreading Rate : 8.0-10.0 Sq.Mtr/Ltr Drying Time : TOUCH HANDLE HARD Curing Time : 6-7 days Overcoating Interval : MIN MAX Flash Point : Above 220C Colour : Grey Finish : Matt Packing : 20 Ltrs (mixed paint) Thinner/Cleaner : Thinner 870 Storage Life : Upto six months as long as the sealed containers are kept under cover in a dry place : Overnight : Indefinite : within 30 minutes : 2-4 hours : Overnight

    RESISTANCE GUIDE Chemical Resistance :


    EXPOSURES SPLASH & SPILLAGE MILD FUMES / OUTDOOR RESISTANCE

    Acids Alkalis Solvents Salt Water

    Good Good Excellent Excellent Excellent

    Good Good Excellent Excellent Excellent

    Temperature Resistance : Continuous : upto 4000 C Intermittent : 4260C Weatherability : Excellent Flexibility : Fair Abrasion Resistance : Excellent - increases with age

    DATA SHEET No. : 164 / rev02 Issue Date : Mar 2009

    under normal temperature conditions.

    Zinc Anode 304 MZS Inorganic Zinc Silicate Coating


    SURFACE PREPARATION
    Remove grease, oil and other contaminants and blast clean to a minimumm of Sa 2.5 Swedish Standard SIS 05 5900 with a surface profile not exceeding 35-40 microns. The surface should be clean and dry before application of Zinc Anode 304 MZS

    APPLICATION
    Stir Part A thoroughly to uniform consistency. Mix the components in the recommended proportion with constant stirring preferably with a mechanical stirrer. Continue stirring until the components are thoroughly mixed. Strain the mixture through a 80 mesh sieve. Allow the mixture to mature for 15-20 minutes before application. Stir again before use and continuously during application. Conventional Spray: Add upto 10% Thinner 870 depending on conditions. Use any standard pressure pot equipment at an atomising pressure of 3.5-4.4 kg/cm2 Airless Spray : Apply preferably without thinning. However, add upto 10% Thinner 870 depending on conditions. Use any 2 . standard equipment having pump ratio 30 : 1. Tip size 0.38 0.48 mm. Tip pressure 110 160 Kg/cm

    TYPICAL PAINTING SPECIFICATIONS

    Surface Steel

    1st Coat Zinc Anode 304 MZS

    2nd Coat Epilux 4 HB MIO

    3rd Coat Epilux 4 CR Enl or Epilux 155 HB or Epilux 89 HB Epilux 5 CTE or Epilux 555 CTE HB Berger Epoxy PU HB or Bergerthane Enl

    4th Coat Epilux 4 CR Enl. or Epilux 155 HB or Epilux 89 HB Epilux 5 CTE or Epilux 555 CTE HB

    Steel

    Zinc Anode 304 MZS

    Epilux 610 Primer Berger Epoxy PU HB or Bergerthane Enl

    Steel

    Zinc Anode 304 MZS

    Steel

    Zinc Anode 304 MZS

    Lumeros HR/47 or Lumeros HR/47 or Silicone Acrylic HB Silicone Acrylic HR Ctg Coating

    Overcoating of Zinc Anode 304 MZS: The surface must be fully cured and free from residual solvent prior to overcoating. This normally takes 10-12 hours but under conditions here humidity is below 80%, the time taken may be longer. While overcoating a mist coat should first be applied to avoid bubbling due to air entrapment.

    Notes :
    1. Use off the mixed paint within the stipulated pot life period. 2. Both components are also available in liquid form for ease of application. 3. The product cures by reaction with moisture and may be applied at high humidity levels provided the blasted surface is free from condensation and meets the requirement of Sa 2.5 Swedish Standard 4. Brush and spray equipment should be cleaned with Thinner 870 otherwise equipment is liable to be damaged 5. At lower relative humidity, drying and curing are likely to be extended. 6. Damaged areas can be touched up with Epilux 4 Zinc Rich Primer Health & Safety : Please refer to the separate Safety Data Sheet available with detailed information.

    DISCLAIMER
    The information contained within this Data Sheet is based on information believed to be reliable at Data Sheet No: 164/ the time of its preparation. The Company will not be liable for loss or damage howsoever caused rev02 including liability for negligence, which may be suffered by the user of the data contained herein. It is the users responsibility to conduct all necessary tests to confirm the suitability of any product or Issue Date : system for their intended use. No guarantee of results is implied since conditions of use are beyond Mar 2009 our control.