Clock Spring Installation

Pipeline Repair Using
Clock Spring
Composite Sleeve Reinforcement
Author: Scott Rukke, Washington Utilities & Transportation Commission
Pipeline companies may periodically find defects in their pipelines during

inspections and normal operation and maintenance. The defect may have been
caused by excavation damage, corrosion, construction errors, or the manufacturing
process. Steel sleeves or repair clamps were typically used to repair pipeline
damage or defects or the damaged section was shut down and replaced. When
properly applied the Clock Spring composite sleeve restores the pipeline to safe
operating condition without having to shut down and replace the pipeline. Clock
Spring composite sleeves are used to make temporary and permanent repairs on
natural gas and liquid pipelines. W.U.T.C. pipeline safety staff inspected and
documented the following example of Clock Spring installation on a damaged
section of pipeline.
Locating Anomaly
The general area of the anomaly

(damage) is excavated based on distance
from a reference point such as a valve or
number of girth welds from the
inspection tool launch point.
Excavation
The pipeline is exposed, the anomaly

located and a preliminary evaluation
conducted.
Pinpointing Anomaly
Exact measurements are taken from a

point of reference such as a girth weld.
The preliminary size and orientation of
the anomaly is documented.
Documenting Pipeline Condition
All information is documented prior to

removal of the wrap or coating.
Coating Removal
The pipeline’s protective wrap or

coating is removed in preparation for
sand blasting.
Sandblasting
The pipeline is sandblasted to a clean

bare metal condition.
Preparation of Pipeline For Evaluation
The sandblasted pipeline is prepared for

an in depth evaluation of the anomaly.
Defect Measurement
The anomaly is measured, documented

and examined for any cracks, grooves or
other imperfections which could affect
the strength of the pipeline.
Defect Evaluation
Precise measurements are taken of the

size of the anomaly. The damaged area
is also examined for any surface cracks
or other strength reducing damage. The
area is photographed.
Depth Measurement
The depth of the damage is measured

and recorded. The damaged area is also
photographed throughout the evaluation.
The damage is evaluated using an
industry recognized criteria to determine
whether the damage can be repaired or
must be cut out.
Ultrasonic Thickness Test
Ultrasonic wall thickness measurements

are taken to evaluate any apparent wall
loss. The damage is evaluated using an
industry recognized criteria to determine
whether the damage can be repaired or
must be cut out.
Magnetic Flux Crack Detection
Since many surface cracks are not

visible to the naked eye a magnetic flux
evaluation is conducted to determine the
extent of any cracks or other strength
reducing imperfections in the pipeline.
Surface Grinding
The damaged area is ground smooth to

remove any gouges or strength reducing
surface cracks.
Final Documentation and Evaluation
The anomaly is further evaluated prior to

the installation of the Clock Spring
repair sleeve.
Ultrasonic Wall Thickness Tests
Ultrasonic wall thickness measurements

are again taken after grinding to measure
actual remaining wall thickness prior to
the installation of the Clock Spring.
Test Fit and Location Marking
The ClockSpring is test fitted and the

location is marked on the pipeline to
ensure that the repair sleeve is centered
around the actual damage on the
pipeline.
Preparing for Clock Spring Installation
A two way tape strip is placed on the

pipeline to hold the Clock Spring in
place while it is wound around the
pipeline.
Filler Material
A filler material is mixed in preparation

to fill in the anomaly on the pipeline.
Filling the Anomaly
The filler material is spread over the

damaged area of the pipeline and around
the two way tape. The tape has a
protective outer layer that keeps the filler
from adhering and will be removed prior
to the start of the Clock Spring
installation.
Preparing Resin
A mixture of epoxy resin is prepared.

The resin is used to adhere the Clock
Spring to the pipeline and to adhere
between the individual layers of the
Clock Spring.
Resin Installation
The resin is spread around the entire

circumference of the pipeline.
Clock Spring Installation
The Clock Spring is adhered to the two

way tape and is wrapped
circumferentially around the pipeline.
Clock Spring Installation
Resin is spread in between each layer as

the Clock Spring is wrapped around the
pipeline.
Clock Spring Tightening
A strap tightener is placed around the

circumference of the Clock Spring and
tightened until all excess resin and filler
is squeezed out of the sleeve.
Final Installation
Strapping tape is placed around the

Clock Spring to hold it while it cures and
hardens. This takes approximately 2
hours.
Primer and Re-Wrap
The pipeline is primered and a protective

wrap or coating will then be re-applied.
Steel straps will be wrapped around the
Clock Spring prior to the final protective
coating being applied.

Clock Spring Installation

Uploaded by

Copyright:

Available Formats

Clock Spring Installation

Uploaded by

Document Information

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Clock Spring Installation

Uploaded by

Copyright:

Available Formats

Pipeline Repair Using

Pipeline companies may periodically find defects in their pipelines during

The general area of the anomaly

The pipeline is exposed, the anomaly

Exact measurements are taken from a

Documenting Pipeline Condition

All information is documented prior to

The pipeline’s protective wrap or

The pipeline is sandblasted to a clean

Preparation of Pipeline For Evaluation

The sandblasted pipeline is prepared for

The anomaly is measured, documented

Precise measurements are taken of the

The depth of the damage is measured

Ultrasonic Thickness Test

Ultrasonic wall thickness measurements

Magnetic Flux Crack Detection

Since many surface cracks are not

The damaged area is ground smooth to

Final Documentation and Evaluation

The anomaly is further evaluated prior to

Ultrasonic Wall Thickness Tests

Ultrasonic wall thickness measurements

Test Fit and Location Marking

The ClockSpring is test fitted and the

A two way tape strip is placed on the

A filler material is mixed in preparation

Filling the Anomaly

The filler material is spread over the

A mixture of epoxy resin is prepared.

The resin is spread around the entire

Clock Spring Installation

The Clock Spring is adhered to the two

Clock Spring Installation

Resin is spread in between each layer as

Clock Spring Tightening

A strap tightener is placed around the

Strapping tape is placed around the

Primer and Re-Wrap

The pipeline is primered and a protective