TEXTILE PROCESSES

The introduction of man-made fibres boosted the development of processing technologies,

which are partly or totally innovative as compared with the world of natural fibres.
Man-made fibres tended initially to superimpose to natural fibres in the various application
sectors, adjusting themselves to the different traditional processes; successively, especially with
the discovery of synthetic fibres, their larger diffusion and the discovery of their potentiality led
to the development of original processes, which allowed to widen the known application fields
and to create new ones.
Some processes (texturing, tow-to-top process, twisting/warping) were connected to such an
extent to fibre typology, that they were carried out, at least in the past, directly within the fibre
production units as final stages of the product to be marketed.

Texturing
Texturing is probably the most typical example of innovative process tightly connected with the
production of continuous filaments, which properties and uses it has thoroughly modified.
As regards man-made fibres, it is estimated that continuous filaments amount to about 55% of
total consumption, divided into apparel (45%), upholstery (31%), industrial uses (13%), carpets
and floorcovering (11%).
The yarn produced through spinning can undergo several processes before its use, as
exemplified in following scheme:



























Textured yarns account for a large part of processed filament yarns. The texturing process
makes up for the inherent deficiencies of a flat continuous filament yarn, both parallel and
twisted, by varying its original textile character and imparting new properties like bulkiness,
covering power, elasticity, soft touch, natural aspect, hygroscopicity and easier processing. In
other words flat yarn, which structure can be compared to iron wires, gains properties which
make it similar to a traditional cotton or woollen yarn.
A textured yarn can be defined as a yarn characterized by effective or latent crimps, waves,
loops of single filaments which, after suitable treatment, can originate properties like bulkiness
and/or elasticity.
In the course of time several processes based on different principles were developed; only a
limited number is at the moment interesting for industrial applications; the process which is by far
the most important is false-twist texturing, whereas the air-jet and compression-chamber
systems are directed to more specific uses.
Following scheme shows a general classification of the various processes.























Textured yarns are in general termed on basis of their production process.
Through the twist-texturing process, following yarns can be obtained:
Highly elastic yarns (stretch yarns), characterized by high crimp elongation (extensibility)
and high crimp contraction; in the case of false-twist process, they are produced by
means of an oven and are named FT (False-twist) yarns.
Set yarns (bulked yarns), characterized by low crimp elongation and low crimp
contraction; in the case of false-twist process, they are produced by means of two ovens
and are named FTF (False-Twist Fixed) yarns.






Description of the texturing systems

Thermo-mechanical processes with deformation through twist

Discontinuous method: twisting-thermosetting-de-twisting

This is the first texturing method ever used: it is based on the thermosetting of a yarn after
twisting with subsequent de-twisting. When this yarn made its appearance in the market in the
30s (in Germany and Japan), it was used for the texturing of viscose. However the users soon
realized that this fibre, owing to its non-thermoplastic nature, was not suited to develop a
sufficiently permanent crimp.
The fibre went through a period of considerable expansion in the 50s, when people realized that
.through such process. thermoplastic fibres like nylon could offer good elasticity and thermal
stability: let us remind in particular the Helanca process for hosiery yarns, which was developed
by the Heberlein company.
The classical method consisted of three discontinuous processes:
Twisting on a twisting machine in 1 or 2 stages through a high number of turns (twists
between 2,500 and 4,500 t/m, i.e. inversely proportional to the linear mass of the yarn).
Twist setting on bobbins by thermal treatment, usually carried out in autoclave with
saturated steam and vacuum-steam cycles (130C temp. for nylon).
De-twisting on a twisting machine, in a first stage zeroing the existing twist and
successively applying a further slight twist in order to improveyarn stability and
regularity.
As a result of the thermoplastic deformation caused by twisting, the single filaments composing
the processed yarn show in the relaxed state a special helicoidal waviness with same direction
as the imparted twist (the applied slight final twists are in fact aimed at reducing the yarn
propensity to rotate on its own axis). This process resulted into yarns with excellent elasticity
(for use in hosiery), but for some end-uses, in particular in case of polyester for knitwear, a
stabilization of elasticity was necessary; to this purpose a further thermosetting stage was
applied on the yarn, which was successively wound on bobbins with a preset tension (stabilized
yarns or set yarns).
A variant of the classical method included:
Separate twisting of 2 yarns with equal number of twists, but with opposite twist
direction (S and Z).
Yarn setting on cones, by means of steam autoclave
De-twisting of the single yarns, down twisting to a level slightly over zero.
Twisting of the 2 yarns together with low twist (e.g. 150/S).
In this way, better balanced textured yarns were obtained.

False-twist method
The previously described process fell into disuse owing to the numerous operations involved, to
its low productivity and to consequent high production costs.
Around mid 50s, a new process proved to be suited to carry out in a single stage (in continuous)
the various operations previously performed separately.
This process is based on the principle of providing the yarn with a false-twist.
If we imagine to take a piece of yarn, to block its two ends and to rotate it in one direction by
sliding it at an intermediate point between the thumb and index of our hand, the yarn segments



placed respectively upstream and downstream that point will receive a twist characterized by a
same number of turns, but showing opposite direction.
If we remove the twisting action by releasing our hold on the yarn, the twist will be set to zero
and the original parallel state of the yarn will be reinstated; in practice this operation has not
produced a real twist, but only a false-twist.
Let us now consider same situation, but with a yarn in motion: the yarn coming out of the
twisting element will have same configuration as the fed yarn. In fact the twist produced in the
zone placed before the twisting element is cancelled by the twist in opposite direction produced
in the subsequent zone.














Now, if in the first zone the twisted yarn is brought into contact with a heating medium (oven)
and is successively cooled (cooling zone), the filaments composing the yarn undergo a
thermoplastic twisting deformation of permanent nature, which is absolutely similar to the one
of previously described discontinuous process.
If we wish to stabilize yarn elasticity, we need to place a second oven after the twisting element.




















False-twist technology, which is by far the most important technology among the various
processes, enjoyed an extraordinary development since its invention: from an initial processing
speed of about 10 m/min, a speed of 1000-1200 m/min was attained (at present the mechanical
speed can reach even 1500 m/min).

















This goal was made possible by improvements brought to all machine elements, but in particular
to the twisting element.

False-twist with hollow spindle
The machines using such system are so-called 1st generation machines.
The twisting device is formed by a hollow tube, in which interior a pin is fixed crosswise; the
yarn is wound around this pin with a complete rotation of 360.















Each rotation of the spindle around its own axis entails the insertion into the yarn of a false-twist
which moves in length direction along the yarn.
Originally, spindles were moved to rotate on ball bearings by friction belts: in this way speeds
of 40.000-80.000 t/min. could be obtained, if wear characteristics of the bearings permitted this.
Later on, mechanical bearings were replaced by magnetic bearings, through which it was

possible to attain spindle speeds up to 900.000 t/min (yarn speed max. 200 m/min). Such high
speeds constitute a limit both mechanically (there are nowadays no mechanical components
working at higher industrial speeds) and processing/technologically (processing wise); in fact
higher speeds would heavily damage the yarn owing to the tensions occurring during the yarn
winding around the spindle pin.

False-twist through friction disks
The limits of the twisting spindle have been overcome with a transmission system in which the
rotating motion is produced by a disk which is almost continuously in contact with the running
yarn (Scragg patent, 1972). In such way, the twist is inserted into the yarn according to a
peripheral speed process and the quantity of theoretical twists applied to the yarn is proportional
to the number of disk rotations and to the disk diameter/yarn diameter ratio.
The system consists of a series of disks mounted on three spindles with their axes spaced out in
such a way, that the disks result partially superimposed; the yarn in motion gets twisted by its
contact with the disks, as it performs a helicoidal evolution around an imaginary cylinder
generated by the superimposition of the disks.














The false-twist aggregate is composed of a disk package placed on a three-axial system, in
which the first disk at yarn entrance and the last disk at yarn delivery simply have the function
of positioning the yarn (guiding disks) without originating any friction, while the internal disks
exert a torsional friction force on the yarn (working disks). The performance of the system
depends on aggregate configuration, on geometry and material composing the disks, on spindle
gauge and on the number of twists applied. Particularly important is the type of material
composing the disks: it must ensure on one hand a good hold (grip) and on the other a good
abrasion resistance.
Basically we can divide the materials into 3 groups: polyurethane and its mixtures (soft and light
material), covered ceramic (with intermediate characteristics) and pure ceramic (more resistant
to abrasion). Disks with soft surface are generally used for PES, especially for fine counts, while
ceramic and covered ceramic disks, which are more widely in use, are intended mainly for PA.
A formula which permits to calculate the twists to be applied on the yarn is the following:








Tdtex = linear mass of drawn yarn (dtex)
f = 1 for traditional process (type FDY)
f = 1,1-1,2 for simultaneous draw-texturization process (POY yarn)

The twist adjustment on the machine depends on the ratio between the peripheral speed of the
friction disks and the yarn speed; this ratio, which is named D/Y, has typically values around
2,0.
The false-twist system with friction disks is at present the dominant process in the texturization
scenario: it ensures the insertion of 2,000.000 t/min in a PES yarn dtex 167 and of up 8,000.000
t/min in PA yarns.

There are however also other interesting industrial processes which apply the friction principle
for linear speed transmission. In particular a widespread system , developed in Japan, makes
use of a device with crossed belts; the yarn, when coming into contact with these belts,
undergoes a twisting action.




















Heating and cooling zones
These zones are an integral part of the false-twist texturization process.
In fact, as already pointed out, the twisting action which the yarn went through in the false-twist
group is transmitted to the preceding yarn path; the oven which is positioned in that zone makes
filaments thermoplastic and is followed by a cooling track which blocks the twisting
deformation.
With the increase of machine speeds,also thes elements experienced substantial improvements.
The primary oven is now composed of a series of grooves or tubes which are arranged in
blocks; these blocks, through which the single yarns run, have a variable length of 1 to 2,5 m
about; are heated by resistors with heat exchange (Dowtherm) fluids, at temperature ranges
which are the higher, the shorter is the permanence time of the yarn in the oven (this time varies
according to the processing speed and to the oven length).




In traditional ovens, temperature may range between 160 and 250 for 2000 mm oven length
and between 200 and 320 for 1400 mm oven length; in all cases, tolerances must be narrow
and strictly controlled (1C inside the oven).
Recently, high temperature ovens (through HT resistors) have been developed; these allow
temperatures up to 500-600C with convection heating, which offers the advantage of reducing
further on oven lengths and of favouring the removal (by combustion) of deposits (finishes,
polymeric remnants) originated inside the oven.
In any case, it is necessary to ensure to the delivered yarn, in the polymer softening zone,
temperatures of 190-210C for PES, 190-205C for PA 6.6 and 165-175 for PA 6.
After leaving the oven, the yarn is cooled down along a path of variable length (1-1,5 m about)
composed of tracks or of metallic plates; cooling takes place through natural circulation of room
air or by active systems, like forced circulation of air, cold air or water. Yarn temperatures at the
exit of the cooling zone (or at the feeding into the twisting aggregate) range between 70 and
100C, depending on the type and on the linear mass of the yarn and on the cooling system.
If a second oven is envisaged, this shall be shorter and have lower operating temperatures.

Draw-texturization
Until the 70s, the texturization required the use of fully drawn yarns (FDY) obtained from
spinning-drawing carried out in two stages.
With the increase of spinning speeds (to 4000-5000 m/min), a partially drawn yarn (POY)
became available, and gave a substantial contribution to the expansion of the false-twist
texturization technology.
In fact this yarn has excellent extensibility during texturization, thus permitting to complete the
drawing on the texturing machine (drawing-texturization). The drawing operation (R= 1.2-1.7)
can be carried out by means of rollers or drawing shafts during the first stage before
texturization (sequential process) or directly in the texturing zone itself (simultaneous process).
This last system is at present the only system used for both PES and PA.

Texturing machines
The machine manufacturer has as primary target the design of a machine which can assure a
stable yarn path (without fluctuations) as well as low and controlled tensions in the zone
included between the draft points situated before the first oven and those after the drawing unit,
in order to attain high production speeds as well as a yarn with good characteristics in terms of
elongation, tenacity, crimp and absence of broken filaments.
Owing to the considerable dimensions of the machine and to the necessity of assembling
various cumbersome parts, also very important are the ergonomic characteristics of the machine
in terms of compactness, accessibility, user-friendliness and maintenance.
Moreover we wish to point out that, whereas guaranteed mechanical speeds reach 1500 m/min,
technological speeds (processing speeds) reach until now about two thirds of that level (higher
speeds can be obtained on PA rather than on PES).
Best performances in terms of productivity and quality require solutions which optimise yarn
path, oven parameters (length, temperature), cooling system (active cooling means),
performance in false-twist insertion (twisting force, tensions, loss of friction heat), take-up
system, continuous monitoring of the process.
These machines are characterised by the presence of only one oven to produce false-twist (FT)
yarns mostly in PA fibre, or by the presence of 2 ovens for the production of false-twist set (FTF)
yarns, mostly in PES fibre and to a lesser extent in PA fibre.
Two-oven machines are in more common use and can of course execute the FT process, while
excluding the setting in the second oven.


From the structural point of view, the machines can moreover differentiate on the basis of their
profile which, in their usual configurations, recall the form of the letters H, M and V.
In the H configuration, the yarn path is almost straight (in the path from feeding device through
oven and cooling until the twisting unit) with consequent low tension levels and less yarn
damage, whereas in the M and V configurations the yarn meets angled points which increase
tensions, but on the other hand can improve path stability.
A two-oven draw-texturing machine for several uses is composed of following parts:
Multilevel creel for bobbins (up to 20 kg each)
Thread cutter with sensor to detect and stop broken threads
Feed shafts in variable number (generally 3 or 4), which fix draft ratios through a yarn
holding system (aprons)
First oven: Dowtherm type (or HT type)
Cooling zone: natural or forced systems
Spindle group: centralized or single position control
Disk combination: variable combination (from 1-4-1 to 1-8-1) with polyurethane or
ceramic disks (diam. 45 mm, h = 6 mm)
Second oven
Contact oiling device with rotating rollers which dip into cups containing the batching
oil (quantity: 1-3%)
Take-up: placed on several levels (3 levels) with bobbin formation (4-5 kg)
Computerized machine control system: setting and control of the various process
Parameters



















































Two-yarns twisting method (duo-twist method)
This method falls within the systems based on thermoplastic deformation through twisting.
It is based on the principle of twisting a piece of 2 yarn ends delivered by 2 feeding units, of
thermosetting the twisted yarn and then de-twisting it on a separating unit, in order to finally wind
up separately the two yarn ends.
It is a process of scarce significance, suitable particularly for the processing of fine counts (also
monofilaments) and characterized by a production speed of 600 m/min.

Thermo-mechanical processes with deformation obtained without twisting
These processes are not based on a principle of twist deformation, but instead on bending,
curving, waving systems which produce yarns with different bulkiness/elasticity properties,
without any tendency to rotate on their own axis.

Mechanical compression chamber method
In this method the yarn is forced by 2 feeding rollers into a heated crimping box and is
submitted to a compression which generates planar bending points (saw-teeth type) on the yarn.
The pressure inside the chamber is regulated by a device which permits the delivery of the yarn
at a constant pressure.
The textured yarn which once used such technology was marketed with the trademark Banlon
(manufacturer: Bancroft); this process is at present no longer in use for textile yarns and has lost
importance also for the production of carpet yarns.
This principle found on the contrary widespread application in the production of crimping boxes
for tow and staple fibre (Fig. 18).





Air-jet compression chamber method
This method can be considered as a development of previously described method: yarn
compression is not exerted mechanically by feeding rollers, but generated by an aerodynamic
system with jets of compressed heated air or of steam.
The warm gaseous stream under pressure enters into a lateral opening of the box, flows into the
yarn guiding channel, pushes the yarn into the expansion box where it is brought to a softening
temperature (plasticization) and is compressed; the result on the yarn is a three-dimensionally
shaped bending.
The exhausted air gets out of leaks placed at the extremity of the box and the yarn is pushed out
of the box.
In order to maintain the properties gained through texturization, the yarn has to be quickly
cooled on perforated drums with air suction down to a temperature lower than glass transition
temperature of the fibre. The yarn reaches the drum through rollers which extract the yarn
accumulated in the final part of the box, or which accumulates in a contact zone between box
and drum (Fig. 64). The process is widely used for the production of carpet yarns in PA or PP
according to BCF technology (Fig. 35).




















Knit-de-knit method
This is a discontinuous method which uses a knitting process on a single-feed small diameter
circular knitting machine; the tubular produced is wound on a support and thermo-set by steam
or straight during the dyeing operation. The yarn is successively unravelled and wound on cones
(speed: abt. 500 m/min). It shows a typical crimp, with wide planar waves of same length as the
stitch.
Owing to its flexibility, this method finds specific uses, in particular in the case of nylon; on the
other hand the process is less suitable for polyester, owing to the poor crimp stability of the
produced yarn.

Blade method
The textured yarn produced with this process was originally labelled with the trademark Agilon
(producer: Milliken); however at present the process is no longer in use, owing to the poor
performance (low crimp stability) of the yarn.

After undegoing direct heat on feeding rollers, the yarn glides under tension on the rounded
edge of a metallic blade following a particular bending angle and is successively cooled on
delivery rollers.
The filaments undergo a structural change due to the compression force exerted by the blade on
their contact side and to the contemporaneous drawing force exerted on the side of the yarn
which is situated on the outside of the blade.
The physical strains generate structural deformations in form of irregular three-dimensional
waves.

Gear method
The yarn obtained with this process was known under the trade name Pinlon; nowadays this
technology has practically negligible importance.
According to this method, the pre-heated yarn gets through two heated and toothed wheels
(speed: up to 600 m/min), between which it is deformed and gets a flat waviness, getting a
geometry which is set and depends on the profile of the wheel teeth.

Mechanical process
Air-jet method
The development of this process was promoted by studies carried out on the effects of
compressed air on yarns (DuPont, 1952); this technology led on one hand to the development of
intermingling systems (with intermittent binding points) for multifilament parallel yarns and on
the other to the production of yarns with modified structural characteristics, which were
originally marketed with the trademark Taslan (from which came the definition taslanized
given to these textured yarns). The principle is based on a jet of a pressurized air directed
hrough a nozzle with a certain angle and turbulence level against a yarn going through the
nozzle; the yarn is overfed, in order to create a compression which has an intensity resulting
from the ratio between feeding speed and delivery speed, which affects the typology of the loops
generated in the yarn.
The air-jet action operates in various phases:
Filament opening at the beginning of yarn feeding into the nozzle.
Creation of a whirl on the open filaments.
Bending of the overfed filaments, with consequent generation of the typical filament
loops which tend to come out of the yarn core.
entangling and setting of the crimped and wavy filaments into a bulky and soft yarn.











The process can be considered as mechanical in case that the air jet is cold; the textured yarn
obtained through a simple aerodynamic stress presents structural characteristics which are
considerably different from those of a false-twist yarn (higher bulkiness, lower elasticity, similar
to traditional yarns).

























The development of this technology is closely connected to the advanced level of the design of
the air-jet nozzle (Fig. 66a).
Since its launch, several nozzle generations have been developed, bearing each time
technological and qualitative improvements; process speed depends essentially only on air flow
speed: the higher is the speed, the quicker is the process.
At the beginning, process speeds of 50 m/min required 20 m3/h of compressed air (which
involved high energy consumption), while nowadays speeds of 500-600 m/min are attained,
with consumption of compressed air (8-12 bar) limited to 5-6 m3/h.




















As the texturization principle is not based on a thermoplastic deformation but is purely
aerodynamic, the process is not limited only to thermoplastic fibres, but can be extended also to
other fibres as cellulose fibres and also glass fibres.
Air-jet texturization ranks at present the second place and holds a 5% share in the market of
false-twist textured yarns.
Its application fields are extremely wide and cover following sectors:
Upholstery and home textiles
Car interior
Sportswear and casual wear
Sewing threads
Technical and industrial articles
Air-jet texturization is at present less productive than false-twist texturization, which fact
hampers economically its application for end-uses which require fine count yarns (finer than
100 dtex).
Air-jet machines are mechanically derived from false-twist machines; besides with air-jet
device, they are equipped with preliminary drawing zones (for POY yarns), with ovens for loop
setting after texturization, and with humidifiers of the yarn at its introduction into the nozzle, to
improve the efficiency of the texturing process.
A machine for universal use is composed of following parts:
Multilevel creel for up to 20 kg bobbins
Thread cutter with sensor to detect and stop possible broken ends
Feed shafts in variable number, which fix draft ratios through a yarn holding system
Fixed heated pins or heated godets, positioned in the drawing zone to heat the yarn
Nozzles (air-jets), placed along with yarn humidifiers at the feed side
Oven: Dowtherm heated oven (length: 1000 to1500 mm, operating range: 140-240C)
Oiling device
Take-up:through centralized system or single take-up positions
Computerized machine control system: setting and control of the various process
parameters.
Figure 66b shows the scheme of an air-jet draw-texturing machine in industrial production

Thermo-chemical processes
These processes are intended for two yarn typologies:
Bicomponent yarns, in which the single filaments are made up by two polymeric
components with different thermal retraction levels. Further to a thermal treatment, they
develop a three-dimensional spiral crimp.
The two components must have a side-by-side (S/S) configuration or a skin-core (S/C)
asymmetrical configuration.
Bi-retractable yarns, composed of 2 groups of filaments with different thermal
properties. This is not a process of effective texturization, as no deformations inherent to
the single filaments are activated, but an effect of bulkiness is generated on the yarn
owing to the different retraction levels of the various filaments.
This principle finds an important application in the production of high-bulk (HB) acrylic
yarns.







































Properties of textured yarns
As already pointed out, textured yarns are characterized by a level of extensibility, elasticity and
bulkiness which is higher than flat yarns (figures 67-68-69 ).
Apart from the several yarn properties which are generally assessed with methods similar to the
methods used for other types of yarn, textured yarns stand out for a property of specific
relevance, which is known as crimp contraction (or crimp elasticity).
This property is essentially assessed on false-twist yarns and is defined as the contraction of a
textured yarn due to crimp development, expressed as percentage rate on the stretched out
(uncrimped) yarn length.
There are several procedure variations, but all of them involve following operational phases:
Preparation of hanks with a certain number of windings.
Latent crimp development in a thermic means (water, air).
1st measurement of the length L0 of the stretched out hank (stretching pre-tension).
2nd measurement of the length L1 of the crimped hank (contraction pre-tension)
Definition of crimp contraction through the ratio (L0- L1)/L0 . 100


































































































































Let us mention some of the most used methods:
Heberlein method
10 m hanks (10 windings) with 1 cN/tex winding tension
crimp development in water at 60-70C for 10 min in the case of PA or in boiling water
for 15 min in the case of PES, with subsequent drying
1st length measurement (L0) on wet hank (at 60C) under 1,8 cN/tex preliminary tension
for 1 min
2nd length measurement (L1) on dried (60C x 60 min) and cooled (60 min) hank under
0,018 cN/tex preliminary tension for 1 min
KK = (L0 - L1)/ L0 . 100

BISFA method
Hanks with 2500 dtex global linear mass (fil.count = 200 dtex) with 2 cN/tex winding
tensions
Crimp development in oven-heated air at 120C for 30 min (PA, PES) and cooling in
standard room conditions for 12 hours
1st measurement (L0) under 2,0 cN/tex preliminary tension for 10 min
2nd measurement (L1) under 0,01 cN/tex preliminary tension for 10 min
Calculation: E = (L0 - L1)/ L0 . 100

On the basis of the crimp contraction values, the yarns can be divided into:
Yarns with high elasticity: E = 35-50%
Yarns with medium elasticity: E = 25-35%
Yarns with low elasticity: E = 25%

Another parameter related to crimp contraction is crimp stability S, which is defined by the
crimp ratio between the crimp of the yarn after mechanical stress and the crimp of the yarn
before the stress:

S = (Crimp contraction after stress / crimp contraction before stress) 100

Twisting

The scope of this operation is the insertion of twists into already formed yarns.
In the case of mono- and multifilament yarns, twisting is applied both on the single components
(ends) and on several components doubled together; in the case of discontinuous yarns, it is
referred only to yarns with 2 or more components (throwing), as the twist insertion into the
single yarns is an operation automatically involved in yarn formation (spinning).
The term twist defines the helicoidal or spiral configuration originated by the rotation of a
yarn or of a bundle of fibres around their longitudinal axis.
The properties related to twist are:
Twist intensity or twist level, which is the twist number per length unit and is usually
expressed in turns/meter (t/m)
Twist direction, which indicates the inclination of the filaments towards the yarn
longitudinal axis and is expressed as follows:
- type S twist: filament inclination from top left to bottom right
- type Z twist: filament inclination from top right to bottom left





























Where:
0= inclination angle
D = yarn diameter in mm
t = turns/m

Yarn twisting can have several targets:
improve dynamometric properties (tenacity, elongation, modulus of elasticity) and
regularity
reduce the tendency of textured yarns to rotate on their own axis and to form loops
improve abrasion and wear resistance
modify structural properties affecting tactile characteristics (touch) and appearance
(crpe effect, covering power, lustre)
improve processing yields by replacing in some cases operations like sizing
In the case of continuous filament yarns, the function of twisting as single filament
protection is replaced by intermingling, an operation in which compressed air is blown
through nozzles against the yarn, thus producing entanglements in the filaments and
formation of cohesion points (false knots); this operation is applied on flat parallel yarns,
both drawn (FDY) and undrawn (POY), and on textured yarns.
Typical twist values which can be found on single continuous filament yarns are:
10-20 turns/m on draw-twisted yarns (cops)
160-800 turns/m for weaving and knitting use
300-500 turns/m for technical/industrial uses (cord)
2000-3000 turns/m for crpe yarns.



























DENOMINATIONS AND REPRESENTATIONS OF SOME YARN STRUCTURES
(according to UNI Standard No. 6699-70)
Twisted single yarn: a continuous filament yarn with only one component (yarn end), on
which a twist is applied
Example:











Doubled or plied yarn: a yarn in which two or more components with same or different
characteristics are doubled together without any twist

Example:













Simple-twisted yarn: a yarn in which two or more components with same or different
characteristics are joined together through just one twisting operation

Example:













Composite-twisted yarn: a yarn in which two or more components with same or different
characteristics are joined together through two or more twisting operations

Example:













In the commercial practice, yarns may anyway be identified with particular denominations based
on typology, composition, structure and application sector.

Twisting technologies
Twisting technologies are based on different working principles (Fig. 71).
According to the two traditional technologies, the twist insertion requires the rotation of the yarn
package around its own axis: if the rotation concerns the package in feed position, the twist is
applied in upwards direction (up-twisting), whereas if the rotation concerns the package in
delivery position, the twist is applied downwards (down-twisting).

























Ring twisting
This is a classical down twist process, which uses the same principle as used in ring spinning,
i.e. a ring element.
The yarn coming from a fixed feed unit situated in upper position runs downwards and is taken
up by rotating spindles through a ring/traveller system.
The feeding bobbin remains stationary, while the receiving bobbin rotates and imparts twist to
the yarn.
Yarn twists are correlated to the angular velocity of the traveller, which runs slightly slower than
the angular velocity of the spindle, in order to permit winding the fed yarn on the package
(bobbin) under formation.
The relation existing between the various parameters is the following:



where:
n = traveller t/min.
n
o
= spindle t/min.
V = yarn feeding speed (m/min)
T = radius of bobbin under formation (m)

Consequently:



where:
T = yarn t/m

The differences between n and n0 are negligible (that is the term V/2pR is negligible) and
anyway by unwinding the yarn from the bobbin in axial direction (overhead unwinding) this
difference is compensated, so that twists are the result of following equation:
T = n
o
/ V

Twisting tensions depend on the type (geometry, material) and on the weight of the traveller,
besides on spindle rotation speed and on the ratio ring diameter/bobbin diameter; anyhow ring
twisting is considered to generate a stiff torsion, which is particularly suited for technical uses.

Twisting with rotating feeding device
This up-twist process is based on the rotation of the feeding package and on the take-up on
stationary bobbin (the rotation of the take-up device has only the function of winding the yarn
on the package).
The yarn is drawn out tangentially from the balloon of the rotating bobbin and assumes twists in
axial direction along a path which, through a thread-guide, winds the yarn on the take-up
bobbin.
Process tensions are essentially controlled by the balloon and the resulting yarn presents a soft
twist; inserted twists are the result of-following equation:

T(turns/m) = spindle speed (turns/min)/ yarn take-up speed (m/min)




Double-twisting
This technique permits to overcome the limits of the two above mentioned twisting principles
deriving from the necessity of rotating at least one yarn package in order to impart the twists: in
fact in this case both the feeding package and the take-up bobbin remain stationary, while the
only moving element is the balloon of the yarn wound on the feeding package.
The double-twist principle (two-for-one-twist) is based on the consideration that a piece of yarn,
after undergoing an U-bending and having rotated around one of the two straight strokes
constituting such letter, gets a first torsion in the descending segment and a second torsion with
same direction in the ascendant segment. Practically in the twisting machine the yarn, while
unwinding from the stationary package, passes through the spindle axis from its top, comes out
of a hole placed at the bottom of the spindle and re-ascends outside the package until it passes
through a pig tail guide and continues its path till it reaches the take-up head.
The double-twist process, which was launched in the 30s for some specific applications in the
industrial sectors (tyre cords), became in these last decades widespread in various textile
applications, largely surpassing above mentioned traditional methods.
In fact this process offers two remarkable advantages:
The insertion of a double twist in relation to spindle speed according to the formula:
T (turns/m) = spindle speed (turns/min)/take-up speed (m/min).2
The possibility of using feeding packages of considerable mass, as there static masses are not
subject to rotating actions; this permits to increase further spindle speeds and to reduce energy
consumption.
From a mechanical point of view, very important is the study of the balloon of the yarn formed
around the package, which is maintained static on a moving system through a magnetic field.
A multipurpose double-twister for continuous filament yarns (both flat and textured yarns) has
generally a double-deck structure with two sides and offers the possibility of mounting different
spindle types with different gauges, thus allowing creeling both of cops and bobbins.
The yarn is guided by an overfeeding roller to the take-up aggregate, which consists of
traversing motion box (thread guide), transmission roller, take-up stand (usually on bicone
bobbins).
Furthermore the machine is equipped with monitoring system for the working parameters.
Indicatively, the machine can reach speeds of 16.000 t/min with take-up speeds up to 200 m/min
and process yarn in counts ranging from 33 to 560 dtex, withtwists from 30 to 2800 t/min.






































































Direct cabling
This is an innovative process which permits to obtain two-component twisted yarns starting
directly from parallel continuous filaments wound on two stationary packages.
The mechanical configuration is somehow derived from the double-twister and the process
develops as follows (Figures 74a-74b):
A first yarn (outer yarn or balloon forming yarn) coming from an outer bobbin is conveyed to
the lower part of the axis of the hollow spindle; a second yarn (feeding yarn) comes directly
from the bobbin housed in the static spindle basket, from which it is unwound in axial direction.
Through spindle rotation the outer yarn, while coming out of spindle basis, creates a balloon
which closes on the adjustment device ((throttle) in the combination point with the feeding yarn,
where twist is generated.
If we wish to obtain a perfectly symmetric twisted yarn, it is essential that the two starting yarns
join together in the twisting point with identical tension and feed levels, in order to avoid
structural unbalances which are termed, owing to their aspect, corkscrew effects.
In the course of the process, the feeding yarn does not receive any twist (excluding the twists
due to axial unwinding), while the outer yarn is subject to a false-twist action, resulting from the
spindle rotation (which generates a twist in one direction) and from the twist produced on the
twisted yarn (twisting with same twist number, but with opposite twist direction).
The consequence is that the yarn obtained with such process presents a very particular
structure:
the two ends are twisted one around the other but not on their own axis, with the filaments of
each yarn end placed in parallel position and perfectly oriented along the yarn axis.
Under this point of view, direct twisting can be defined as the operation which maintains
unchanged in the assembled yarn the morphology of the single components.



























Direct twisting, owing to quality and productivity reasons, tends to replace, in the production of
tyre cord and of industrial twines, the traditional two-stage technique composed of the twisting
the parallel single yarns and of the subsequent throwing (of 2 or more doubled yarns) with equal
number of turns with opposite direction.
The twists imparted to the yarn are the result of the ratio between the spindle speeds (t/min) and
the take-up speed (m/min): the machines can work at 10,000 t/min with feed and take-up
bobbins weighing up to 10-15 kg; the yarn counts used for technical applications range from 940
to 2100 dtex, the inserted twists from 150 to 600 t/m.


Yarn covering
Yarn covering or yarn wrapping is a process which winds one or more yarns (sheath) around
another yarn (core) without imparting any twisting effect.
Covered yarns can be of two types: single-covered (core yarn + textile yarn) wound in S or Z
direction (Fig. 75a) or, to ensure a perfect twist balancing, double-covered (core yarn + two
textile yarns wound in opposing directions (Fig. 75b)).





















This operation can have different purposes:
Protection and improvement of the mechanical characteristics of the core yarn (resistance to
abrasion and to tensile stress)
Modification of the structural properties in relation to tactile (touch, softness, bulkiness) and
optical (colour effects) exigences, for instance for the production of fancy yarns
Control of core elasticity, in the case of elastane yarns.
Covered yarns belong to a more generic yarn class of corespun yarns, generally composed by
an elastane core and by sheath yarns of different nature wound with various techniques. Out of
these techniques, only hollow spindle throwing (used with doubled cotton yarns) makes use of
same principle as covering machines.
The operation principle is the following:



The core yarn coming from a feeding bobbin is passed, under a precisely set tension, through
the perforated axis of the spindle and is wound on take-up tubes. At the same time the spindle is
rotated together with a package of covering yarn, which winds spiralwise the core yarn passing
through the spindle axis.
Machine configuration may envisage only one operating spindle, in which case a single
covering (S.C.) is carried out, or have two spindles in series with axial ranging, in which case
the operation is named double covering (D.C.).
Some relevant application sectors (ladies hosiery , sock welts, elastic fabrics, bandages, laces)
use covered yarns composed of elastane core yarn and textured covering yarn; another sector
of high interest is that of fancy yarns, where the core element can consist of rigid yarns.




































A typical process for the production of elastane-covered yarns shows following components:
Positive unwinding system (roller device) for the elastomer yarn fed by the package.



Preliminary drawing zone controlled by a feeding unit with grooved disks. Preliminary
drawing is usually required for yarns with a linear mass higher than 156 dtex (ratio 1,3
approx.).
Lower or 1st spindle (S or Z twist) rotating at variable speeds (27,000-12,000 t/min)
depending on the weight of the flanged bobbin (300-1000 g according to linear mass). The
S.C. yarn results unstable and has tendency to become curly.
Upper or 2nd spindle (in the case of D.C. yarn, twist direction is the opposite of the 1
st

spindle). In order to obtain a balanced yarn, it is necessary that the twists (speeds) of the 2
nd
covering yarn are lower (20-30%) than those of the 1st covering yarn; in fact the 2
nd
covering
takes place over a yarn of larger diameter, therefore the balancing is obtained only when the
same yarn length has been wound on the final bobbin.
Drawing or tensioning: this operation produces the main part of the draft of the elastane
yarn. It is carried out by feeding units with grooved disks or by rubber rollers as balance
weights. Depending on linear masses, the total draft ratio (preliminary draft + main draft)
may vary from 3 (with fine yarns 10 dtex) to 5,8 (with coarse yarns 300 dtex).
The number of windings per linear meter of core yarn depends on the rotation speed of the
spindles (t/min) and on the transition speed of the core yarn (meters/min)
Take-up on bobbins (max. speed 60 m/min) with cylindrical or also conical tubes. A
decisive role for the subsequent processes is played by the perfect winding conformation of
the winding, which has to show long and crossed pitch and tapered bobbin borders.

The linear masses of the covering yarns (PA, PES) for the production of ladies hosiery, support
hoses and welts of mens socks, range between 8 and 110 dtex, while linear masses of elastane
yarns range from 10 to 450 dtex; the twists applied (in case of ladies stockings) range from 600
to 1800 t/m for S.C. yarns, and total twists for D.C. yarns range between 1800 and 2500 t/m (S +
Z).

Twisting + texturing in a single phase
Among the various types of twisted yarns, yarns characterized by a high number of twists
(2000-3000 t/m) have particular market significance.
These yarns, which are known as crpe yarns and were originally developed for the silk
industry, stand out for some peculiar properties with, both tactile (springy and stiff touch, crease
resistance) and aesthetical (lustre and silky appearance). which they provide to the fabrics.
As polyester yarn (linear mass 44 to 78 dtex with filaments of medium fineness) is one of the
most widely used man-made fibres, we have selected Fig. 77a is to illustrate a process which is
specifically related to this fibre.
The traditional process consists of two phases:
Twisting with double-twister under operating conditions, like size of feeding/take-up
packages and machine regulations, which are suited to produce a yarn with good crpe
effect, without any irregularity and wound on bobbins of uniform shape and density.
Twist setting: this operation, which consists of thermosetting yarn twists, is absolutely
necessary for twisted yarns with unbalanced structure. It is a delicate process, which is
carried out by submitting the bobbins in an autoclave to vacuum-steam cycles (at 120C); it
is of primary importance that the thermal action develops uniformly on the whole yarn
package, in order to avoid dyeing unevenness caused by affinity irregularities and by
residual thermal retraction of the fibre.




A recently introduced alternative method permits to produce yarns with characteristics similar to
those of the traditional method (the objective is to imitate silk crpe items) and consists in
submitting the yarn to a continuous process including twisting, thermosetting and texturization.
The machine is composed essentially by following aggregates/working phases:
Twisting yarn from cops on a double-twister. The twist to be applied on the yarn is lower
(600-1500 t/m depending on the linear mass) than the typical twist of traditional crpe
yarns.
Ceramic disk feeders with tension control, placed on two shafts, one of which on the
feeding side and the other on the take-up side of the texturization machine .
Heating oven with diathermic oil (200-220C).
Texturization units with false-twist spindles placed on magnetic bearings (speed
200,000-250,000 t/min, twists 2700-3900 t/m). It is noteworthy, that in this case an
outdated false-twist system is used; this is due to the fact, that the friction system is not
suited to above said operation.
Oiling system
Take-up aggregate for up to 3 kg bobbins.

Besides running the whole process, the machine can operate also as simple twisting machine
(bypassing the oven and spindle units), or as twisting and thermosetting machine (bypassing
only the spindle unit).































Air entangling (air covered yarns)
Air entangling is a process which permits assembling together in a single bobbin two or more
yarns of same or different nature and count, with or without including elastomer yarn. The
bobbins thus produced can be used directly in knitting, hosiery knitting or weaving.
Special elastic properties can be imparted to the manufactured items through the insertion of the
elastomer fibre. Fig. 77b shows the sequence of the process as follows:
The yarn which is unwound by the feeding package (1a) runs through the yarn scanning sensor
(3), is wound 2 or 3 times around the feeding roller (5) in order to keep tension as much as
possible under control. The yarn coming out of the roller crosses the proper thread guides and
enters the jet nozzle.
The elastomer yarn, owing to its lower winding speed on roller (2), is wound 1 or 2 times on the
feeding roller (4) which rotates at higher speed in order to draw the yarn while interlacing. The
yarn continues its run, passes through the yarn scanning sensor and reaches the jet nozzle. In
case of interlacing with the third thread, the yarn coming from the feeding package (1b) passes
through the yarn scanning sensor and is wound 2 or 3 times around the feeding roller (4). In the
subsequent course, the yarn is plied together with the other yarns, and all of them enter the jet
nozzle to be interlaced. The yarns coming out of the jet nozzle are wound 2 or 3 times around
the feeding roller (7) which has the task of lowering and stabilizing the tension of the interlaced
yarns. The roller delivers the yarns to the take-up tube, not before crossing the oiling roller (8).
The final tensioner (9) adjusts the tension on the level to be obtained in the take-up zone.































Production of discontinuous fibres
The processing of man-made fibres on traditional spinning systems requires the production of
fibres of definite length which are also named, on the basis of their length, short staple fibres in
the case of fibres to be spun on cotton spinning system, and long staple fibres in the case of
fibres for worsted or woollen spinning.
Staple fibres are obtained from a semi-finished product, a cable of filaments named
tow,through processes which obviously have no precedent in the processing chain of natural
fibres.

Tow conversion into staple fibre
This process, which is by far the most used and is generally placed in the final stage of the fibre
production lines, employs mechanical cutting devices, named staple cutters.
During the time, various fibre cutting systems were developed, but only few are now still
operative, at least for the production of standard staple fibre for textile use.

Lummus staple cutting machine
The operating system of this machine, although based on a simple principle, is in a position to
ensure cost-effective performance and good product quality, which fact led this technology to a
widespread application.
Cutting takes place by compressing the filaments against blades placed perpendicularly to the
longitudinal axis of the fibres.
The tow, which is properly stretched in order to line up the filaments and to remove crimp, is
fed to a wheel, which shows on its border radially fixed knife blades. While rotating, the tow
winds up around the wheel blade and comes into contact with a pressure roller placed outside
the tow. With the increasing of the winding number and consequently of tow thickness, the
sliver is pressed by the pressure roller until the internal filament layers are cut by the blades
facing them and discharged downwards in form of staple fibre.
The cutting process is studied in a way as to keep constant the thickness of the tow wound on
the wheel. The fibre length is brought about by the distance between the knives; the cut is
uniform, unless problems of excessive wear or blade damages arise (Fig. 78).





















Gru-gru staple cutting machine
Gru-gru is the name of a cutting system composed of rotating blades cutting the fibre tow
retained by some clamping points and glidings perpendicularly to them.
The device consists of two adjacent wheels, placed on horizontal parallel axis and provided with
gummed teeth staggered by empty spaces.
Between the wheels, which rotate in opposite direction, the strained tow is fed from the upside
and is clamped by the holding points constituted by the wheel teeth; a wheel with rotating
blades moves in synchrony transversely to the tow flow and, while passing through the empty
spaces, cuts the filament bundle which is clamped between the wheel teeth.
The fibre length (staple length) corresponds to the distance between the interstices (that is to the
distance between the teeth).
This process, which finds limited application, presents some limits due to its mechanical
complexity, to the quick wearing out of the knives (with consequent need of frequent
replacement) and to its irregular cut due to the not perfect hold of the fibres between the
clamping points.

The cutting machines must be capable of operating in line with the working speeds (up to 200-
300 m/min) and with the linear masses (up to 3-4.106 dtex) coming from tow production lines.
The range of the lengths of the produced fibre tufts has to comply with the requirements of the
various processing sectors; in the case of traditional spinning systems, fiber length ranges are
the following :
28-40 mm for traditional cotton spinning system
40-60 mm for modified cotton spinning system
60-80 mm for carded (woollen) spinning system
80-120 mm for worsted (woollen) spinning system
120-200 mm for semi-worsted (woollen) spinning system

The quality characteristics of a staple length must comply with strict tolerances in terms of
deviation from the nominal cut length (both as average value and as variation coefficient), of
absence of long staple fibres (e.g. >20% against the normal level) and of double or multiple
cuts.
The presence, even if in minimal percentage, of fibres with anomalous length in the bales to be
processed on cotton spinning system can seriously jeopardise the spinning behaviour and the
quality of the production.
These anomalous fibres are due either to the cutting operation or to an irregular tow
conformation (filament bundles protruding from tow core), or also to defects in the cutting
machine (damaged or lacking blades).

Staple fibres are normally characterized by fibres of same length (square cut); in case that
subsequent processes require this, , staple fibres of different square cuts may be properly
blended together in order to get a staple with variable cut length.

Tow-to-top conversion
This term defines the direct transformation of a cable of continuous filaments (tow) into a sliver
of discontinuous fibres (top).
During this operation, fibre alignment does not get lost as it happens in case of machine cutting,
in which tow filaments are cut and placed in bulk into the bale (staple fibre). This technology is




de facto limited to the woollen spinning system, which requires the use of fibres with variable
length diagrams (that is similar to wool).

Tow-to-top stretch breaking technology
This technology is based on a simple principle, which consists in drawing the tow gradually in a
controlled way until the breaking point of the fibres is reached; this breakage takes place within
operating zones (drafting zones) composed of a series of drafting assemblies which originate a
sliver with triangular-shaped fibre diagram, also called shoe-shaped diagram.
This process finds its optimal application in the processing of acrylic fibre, in view of its
inherent characteristics and of its suitability for particular applications viz. end-uses.. The
acrylic fibre is in fact characterized by a relatively low breaking strength compared to other
fibres (as PES and PA), which fact permits the use of a tow with very high linear mass;
moreover it has the propensity to deform under stress (particularly in warm conditions),
maintaining this deformation in a metastable (retractable) state till a subsequent thermal
treatment, which restores the original state of the fibre (i.e. set or retracted), takes place.
Thanks to this peculiarity, the fibre finds an important application in the production of yarns
composed of shrinkable and set fibres (HB or High Bulk yarns) which, owing to their different
retraction levels, are in a position to develop a high bulkiness after a thermal treatment. The
production lines are generally composed of 2 passages: a stretch breaking machine and an
integrated drawing frame.
For some types of production (big lots, mixtures of several fibres, dyed fibres), the line may
consider the presence of a third passage composed of a simple pin drafter.
The two passages line includes following machines:

Tow-to-top stretch breaking machine
This machine has only one operating side and the tow path is of linear type (on a single level
see Fig. 79) or works on two levels. It is composed by following units:
Feeding creel:
The tow (1 or 2 tows) reaching the machine must be regular, centred, open and stretched,
without entanglements and distortions. This result is ensured by the support of opening and
guide devices and requires a sufficiently long tow path, in order that the material coming
from the bales (placed before or after the machine body) arrives from the top at the feeding
point after passing through a series of bars mounted above the machine.
Modules for preliminary drawing, drawing and stretch breaking
The considerable linear mass of the tow requires drawing heads of adequate strength and hold,
composed of cylinder aggregates with different conformation and coupled with pressure rollers.
The first draft zone (length 1,5 m approx.) is characterized by the presence of 2 plates with
adjustable heating temperature, which heat the fibres running through it, thus favouring their
drawability. The applied draft must only extend the filaments, without causing their break.
The temperature attained by the fibre (normally higher than glass transition temperature) and the
draft ratio give rise to the final retraction of the fibre.
The second draft zone (long draft zone), which has a length similar to preceding zone, carries
out a preliminary stretch breaking to produce fibres of a length comprised between 1 and 4 m.
The second draft zone is followed by the end draft zones, composed of 3 drawing heads, the
second and third of which are mobile to enable modifying the gauges and setting the
characteristics of the fibre diagram.
Other machines are equipped also with a cooling system for rollers and pressure rollers by
means of internally circulating cooled water.



While leaving the last breaking zone, the sliver is consolidated by an air-jet nozzle and then
conveyed to the crimping box, which is composed of 2 calenders and of a crimping box.
A device for continuous and linear steaming follows to permit, if necessary, a total retraction of
the fibres (at 110-115); the sliver or the top is then collected into cans, through automatic
canchanging.
Technical data of a modern tow-to-top stretch breaking machine
Linear lay-out (on 1 level) with only one operating side
Heads of preliminary drawing, drawing and stretch breaking: No.6
Total linear mass of fed tow (1 or 2 tows): max. 240 ktex
(on basis of acrylic fibre 3,3 dtex)
Linear mass of filaments 0,8-17 dtex
Average staple length of stretch broken fibres 80-130 mm
Delivery speed max. 350 m/min
Linear mass of delivered slivers 20-60 ktex
Effective output per hour 350-500 kg/h
Machine overall dimensions (length) 11,5-12 m




















Integrated drawing frame
This machine completes the process and has the task of plucking, mixing and regularizing the
slivers through an effective doubling and drawing action.
This passage performs the mixing of steam-set slivers with shrinkable slivers in order to obtain a
HB (High-Bulk) top; as the two types of slivers are usually doubled in equal number of slivers,
the delivered sliver weight (assuming a 20% retraction of the steamed component) is composed
by about 55% steam-set fibres and 45% shrinkable fibres.








The machine is constituted of two parts placed in sequence (Fig.80):






















V = drawing speed
D = draft
G = draft gauge
V2 > V1


















Preliminary drawing module, which has several drawing aggregates (each of them composed
of a couple of rollers and of a pressure roller) with independently adjustable draft ratios and
gauges.
Drawing frame with pin head (gill-box) with rotating flanges or control chain .

The combined drawing action of the two modules permits to obtain a multiplying effect which
increases the total drawing capacity by 24-30 times, with consequent higher doubling number
and improved mixing level.

Technical data of a modern integrated drawing frame
Feeding batch max. 1000 ktex
Total draft (preliminary draft of 1st, 2nd, 3rd, 4th zone) 2,5 3,5
Feeding speed max. 80 m/min
Delivery speed max. 500 m/min(cans)
400 m/min (bobbins)
Doubling number (creels with cans or bobbins): 24-32-36
Can, bump or bobbin delivery
Electronic autoleveller


Tow -to-top cutting technology
This technology, although based on a since long time established principle, finds even today
very limited application. The tow, which should be of regular shape and uniform thickness, runs
between a rotating upper roller equipped with an helical blade (cutting roller) and a lower
pressure roller (called anvil).The exerted pressure crushes the fibres level with the blade, until
they are cut: the length and variability of the cut are brought about by the blade pitch (Fig. 81).
his process finds some specific uses (sewing threads, technical yarns) in case of filament cables
characterized by high tenacity properties (PES, PA, PP). In fact the cutting technique preserves
fibre properties, in particular dyeing evenness and dynamometric characteristics.
The basic element of the process is obviously the cutting roller, which blades must ensure a
sufficiently clear cut of fibre ends (absence of burrs and agglomerations) along with good
resistance to wear and to stress.









































The typology of the fibre diagram can be adjusted by varying the roller pitch or the angle of the
feeding tow in respect to the roller (Fig. 82); in any case a fibre diagram is obtained which
shows lower inclination than the typical diagram of wool or broken top (Fig. 83).































Scheme of a modern tow-to-top cutting machine (cut converter)
The feeding batch is generally formed by two tows which are placed behind the machine and are
conveyed, by means of guide bars and tension rollers, to the cutting aggregate. Attention has to
be paid so that the material reaches the cutting roller in form of a regular sliver with parallel,
stretched and well opened filaments.
An intersecting head opens the fibres and distributes them uniformly, thinning the sliver;
successively a crimping device consolidates the sliver, which is finally collected into cans.

Technical data
Total linear mass (1 or 2 tows) max. 240 ktex
Linear mass of single filament 1,3-17 dtex
Average fibre length 75-88-105 mm
Delivered sliver 15-30 ktex
Mechanical feeding speed 280 m/min
Effective output 250-350 kg/h
Overall dimensions 4,5 x 14,5 m

Bibliographic sources (also for the figures):

Man-made Fibres RW Moncrieff
Physical Properties of Textile Fibres Morton, Hearle
Dictionary of Man Made Fibers HJ Koslowsky
Fibre Tables accrding to P.A. Kock ITA
Le Fibre Chimiche Cazzaro, Colombo Snia Ricerche
Polyester The Textile Institute
Synthetic Fibers Fourn
Handbook of Yarn Production P. Lord
Chemical Fibres International (magazine)
Specifications by BISFA ISO UNI
Assofibres reports
Technical bulletins of producers and manufacturers
SEM photographs supplied by Centro Tessile Cotoniero e Abbigliamento