Non-Ferrous Metals

Download as pptx, pdf, or txt
Download as pptx, pdf, or txt
You are on page 1of 26

NON-FERROUS METALS

NON-FEROUS METALS
 No iron present
 More resistant to corrosion than ferrous metals
 Ideal for gutters liquid pipes, roofing and outdoor signage
 it’s major advantage to ferrous is its malleability
generally more costly than ferrous metals
 used widely in residential, commercial and industrial industry
PROPERTIES
low strength at high temperature
 suffers from shortness
 more shrinkage than ferrous metals
NON-FERROUS METALS
ADVANTAGES:
 high corrosion resistance
 easy to fabricate (machining, welding, forging and rolling)
 possess very good thermal and electrical conductivity
 attractive color and low density
COPPER
One of the most widely used non-ferrous metals in the industry.
Soft, malleable and ductile material with a reddish-brown appearance.
With a specific gravity of 8.9 and melting point of 1083°C
Corrosion resistant metal
PROPERTIES AND USES
1. High Thermal Conductivity –heat exchange, heating vessels and appliances, etc.
2. High Electrical Conductivity – used as electrical conductor
3. High Ductility – easily cold worked, folded, spun
4. Good Corrosion Resistant – used for providing coating on steel prior to nickel
and chromium plating
ALUMINIUM
White metal produced by electrical processes from clayey mineral known as
Bauxite.
Light metal having a specific gravity of 2.7 and melting point of 658°C
In its pure state, the metal would be weak and soft for most purposes but when
mixed with small amount of other alloy, it becomes hard and rigid.
It may be blanked, formed, drawn, turned, casted and forged.
PROPERTIES AND USES
1. Corrosion resistant
2. Good conductor of heat and electricity
3. Possesses high ductility and lightweight (used in aircraft and automobile)
4. Needs frequent annealing if cold worked since it becomes hard.
ALUMINIUM
5. Can replace copper to some extent in electrical transmission due to its
ductility and malleability
6. It is used in manufacturing of household utensils, its non-toxicity makes it a
useful metal for cooking utensils under ordinary condition and thin foils are
used for wrapping food items
LEAD
Lead is the heaviest of the common metal.
Lead is extracted from its ore known as galena.
It is a bluish grey metal having specific gravity 11.36 and melting point 326°C.
It is so soft that it can be cut with a knife. It has no tenacity.
It is utilized in manufacturing of water pipes, coating for electrical cables, etc.
Properties and Uses
1. It is resistant to corrosion and many chemicals do not react with it (even acids).
2. It is soft, heavy and malleable, can be easily worked and shaped.
3. Lead is utilized as alloying element in producing solders and plumber’s solders.
4. It is alloyed with brass as well as steel to improve their machinability.
TIN
It is a brilliant white metal with yellowish tinge. Melting point of tin is 240°C
It is soft, malleable and ductile. It can be rolled into very thin sheets.
It is used for making important alloys, fine solder, as a protective coating for iron
and steel sheets and for making tin foil used as moisture proof packing.
Properties and Uses
1. It is used for tinning of copper and brass utensils and copper wire before its
conversion into cables.
2. It is useful as a protective coating for iron and steel since it does corrode in dry
or wet atmosphere.
3. It is utilized for making important alloys such as fine solder and moisture proof
packing with thin tin sheets.
ZINC
 The chief ores of zinc are blende (ZnS) and calamine (ZnCO3).
 Zinc is a fairly heavy, bluish-white metal principally utilized in view of its low cost, corrosion
resistance and alloying characteristics.
Melting point of zinc is 420°C and it boils at 940°C.
Properties and Uses
1. High corrosion resistance: Widely used as protective coating on iron and steel. Coating may
be provided by dip galvanizing or electroplating.
2. High fluidity and low melting point: Most suitable metal for pressure die casting generally in
the form of alloy.
3. When rolled into sheets, zinc is utilized for roof covering and for providing a damp proof non-
corrosive lining to containers.
4. The galvanized wires, nails, etc. are produced by galvanizing technique and zinc is also used
in manufacture of brasses.
NICKEL
Properties and Uses
1. About at least 85% of all nickel production is obtained from sulphide ores.
2. Pure nickel is tough, silver coloured metal, harder than copper having some but
less ductility but of about same strength.
3. It is plated on steel to provide a corrosion resistance surface or layer.
4. Widely used as an alloying element with steel. Higher proportions are
advantageously added in the production of steel such as monel or in conel.
5. It possesses good resistance to both acids and alkalis regarding corrosion so
widely utilized in food processing equipment.
MAGNESIUM
Properties and Uses
1. Principal ores of magnesium are magnesite, carnallite and dolomite.
2. Magnesium is extracted by electrolytic process.
3. It is the lightest of all metals weighing around two-thirds of Al.
4. The tensile strength of rolled annealed Mg is same as that of good quality cast Fe.
5. Magnesium can be easily formed, drawn forged and machined with high accuracy.
6. In powdered form it is likely to burn, in that situation adequate fire protection
measures should be strictly observed.
7. Its castings are pressure tight and achieve good surface finish. Magnesium castings
include motor car gearbox, differential housing and portable tools.
VANADIUM
Properties and Uses
1. It occurs in conjunction with iron pyrite, free Sulphur and carbonaceous
matter. It is silvery white in colour.
2. Its specific gravity is 5.67. Its melting point is 1710°C.
3. When heated to a suitable temperature it can be hammered into any shape or
drawn into wires.
4. It is used in manufacture of alloy steels.
5. Vanadium forms non-ferrous alloys of copper and aluminium from which
excellent castings can be produced.
ANTIMONY
Properties and Uses
1. Chief ore of antimony is stibnite. To a small extent, antimony is obtained as a
by-product in refining of other metals such as lead, copper silver and zinc
2. It is silvery white, hard, highly crystalline and so brittle that it may be readily
powdered.
3. Its specific gravity is 6.63 and melting point is 630°C.
4. It is generally used as an alloying element with most of heavy metals.
5. Lead, tin and copper are the metals which are most commonly alloyed with
antimony.
CADMIUM
Properties and Uses
1. Cadmium It is obtained commercially as a by-product in the metallurgy of zinc
and to some extent of lead. White metal with bluish tinge, capable of taking a
high polish.
2. Its specific gravity is 8.67 and melts at 321°C. It is slightly harder than tin but
softer than zinc.
3. It is malleable and ductile and can be readily rolled and drawn into wires. It is
chiefly utilized in antifriction alloys for bearings, used as rust proof coating for
iron and steel, components of automobiles and refrigerator such as nuts, bolts
and trimmings, locks and wire products are plated with it.
TITANIUM
Strong and lightweight refractor metal
Critical to aerospace industry, medical, chemical and military aplications
Exceptional corrosion resistant by both water and chemical media
Non-magnetic and biocompatible (non-toxic and non-allergenic) which has
led to its increasing use in medical field
NON-FERROUS
ALLOYS
COPPER ALLOY
Copper alloys are among the best conductors of heat and electricity and they have
good corrosion resistance.
BRASS
All brasses are basically alloys of copper and zinc.
The tensile strength and ductility of brass both increase with increase in content of
Zn but ductility of brasses drops significantly.
βphase is less ductile than α-phase but it is harder and stronger.
There are various types of brasses depending upon proportion of copper and zinc.
(1) Alfa brass: Contains up to 36% Zn and rest Cu for cold working.
(2) Alfa-Beta brass: Contains 36 to 45% Zn and remainder is Cu for hot working.
COPPER ALLOY
Suitable type of brasses can undergo the processes of casting, hot forging, cold
forging, cold rolling into sheets, drawing into wires and extrusion to obtain
requisite cross-section bars.
Brass has a greater strength than that of Cu but has a lower thermal and electrical
conductivity.
Brasses possess very good corrosion resistance and can be easily soldered.
Brasses are used in hydraulic fittings, pump linings, utensils, bearings and bushes,
etc.
BRONZE
The alloy of copper and tin are usually termed bronzes. The useful range of
composition is 75 to 95% copper and remainder tin.
COPPER ALLOY
It possesses superior mechanical properties and corrosion resistance to brass.
The alloy can be easily cold rolled into wire, rods and sheets.
With increase in tin content, the strength of this alloy and its corrosion resistance
increases. It is then known as hot working bronze.
Bronze is generally utilized in hydraulic fittings, bearings, bushes, utensils, sheets,
rods and many other stamped and drawn products.
ALUMINIUM ALLOY
Aluminium may be alloyed with one or more alloying elements such as copper,
manganese, magnesium, silicon and nickel. The addition of small quantities of
alloying elements converts the soft and weak aluminium into hard and strong
metal, while it retains its light weight.
DURALUMIN
A famous alloy of aluminium containing 4% copper, 0.5% manganese, 0.5%
magnesium and a trace of iron with remainder as aluminium.
It possesses high strength comparable with mild steel and low specific gravity.
Its corrosion resistance is much lower as compared with pure aluminium.
ALUMINIUM ALLOY
The strength of this alloy increases significantly when heat treated and allowed
to age for 3 to 4 weeks it will be hardened (age hardening).
To improve upon the corrosion resistance of it, a thin film of aluminium is rolled
on the duralumin sheets (Alclad) used in aircraft industry.
It is widely utilized in wrought conditions for forging, stamping, bars, tubes and
rivets.
It can be worked in hot condition at 500°C. However, after forging and
annealing it could also be cold worked.
Due to light weight and high strength this alloy may be used in automobile
industry.
ALUMINIUM ALLOY
Y-ALLOY
It is also known as copper-aluminium alloy.
The addition of copper to pure aluminium improves its strength and
machinability.
Y-alloy contains 93% aluminium, 2% copper, 1% nickel and magnesium. This alloy
is heat treated as well as age hardened just like duralumin.
Since Y-alloy has better strength at elevated temperature than duralumin
therefore it is much used in aircraft cylinder heads and piston.
It is also used in strip and sheet form.
ALUMINIUM ALLOY
MAGNALIUM
It is produced by melting the aluminium 2 to 10% magnesium in a vacuum and
then cooling it in vacuum or under a pressure of 100 to 200 atmospheres. About
1.75% copper is also added to it.
Due to its light weight and good mechanical characteristics, it is mainly used for
aircraft and automobile components.
HINDALIUM
It is an alloy of aluminium and magnesium with small quantity of chromium.
It is manufactured as rolled product in 16 gauge mainly used in manufacture of
anodized utensils.
NICKEL ALLOY
GERMAN SILVER
The composition of this alloy is 60% Cu, 30% Ni and 10% zinc.
It displays silvery appearance and is very ductile and malleable.
It is utilized for electrical contacts, casting of high quality valves, taps and
costume jewellery. It is also used in producing electrical wires.
MONEL METAL
It contains 68% Ni, 30% Cu, 1% iron and remainder small additions of Mn and
other elements.
It is corrosion resistant and possesses good mechanical properties and maintains
them at elevated temperatures.
NICKEL ALLOY
NICHROME
It consists of 65% nickel, 15% chromium and 20% iron.
It has high heat and oxidation resistance. It is used in making electrical
resistance wire for electric furnaces and heating elements
It is an alloy of nickel and chromium which is utilized as heat resistant electrical
wire in electrical applicances such as furnaces, geysers and electric iron, etc.
GOLD AND ITS ALLOY
Gold is really an alloy or mixture of metals. The purity or fineness of gold is
indicated in karats number (24 K). Gold that is 24 K is also called fine gold and is
greater than 99.7 % pure gold. Gold will form alloys with most metals such as
silver, coper, and zinc.
GOLD ALLOY ALLOY COMPOSITION
Yellow Gold (22K) Gold (91.67%), Silver (5%), Copper (2%), Zinc (1.33%)
Red Gold (18K) Gold (75%), Copper (25%)
White Gold (18K) Gold (75%), Platinum/Palladium (25%)
Soft Green Gold (18K) Gold (75%), Silver (25%)
Blue Gold (18K) Gold (75%), Iron (25%)
Purple Gold Gold (80%), Aluminum (20%)