11 IV April 2023

https://doi.org/10.22214/ijraset.2023.50704
 International Journal for Research in Applied Science & Engineering Technology (IJRASET)
ISSN: 2321-9653; IC Value: 45.98; SJ Impact Factor: 7.538
Volume 11 Issue IV Apr 2023- Available at www.ijraset.com

Properties of Autoclaved Aerated Concrete in

Different Curing Conditions: A Review
Jayakrishnan K1, Indu Susan Raj2, Dr. Elson John3
1 2 3
PG Student, Women Scientist, Associate Professor, Dept. of Civil Engineering, Mar Athanasius College of Engineering,
Kothamangalam, Ernakulam, Kerala, India

Abstract: Autoclaved aerated concrete (AAC) has many benefits for structures, such as heat insulation, sound insulation, fire
resistance, reduced dead weight, and many more. AAC products include blocks, wall panels, floor and roof panels, and lintels.
Besides its insulating capability, one of AAC's advantage in construction is its quick and easy installation since the material can
be routed, sanded, and cut to size on-site using standard carbon steel band saws, hand saws, and drills. Although AAC has been
produced for many years, there are still some points that need to be clarified. One of these points is the effect of humidity
intrusion on AAC members in areas with high relative humidity levels, like Mediterranean climates. Therefore, various tests
associated with the mechanical and physical properties of AAC concrete should be carried out, particularly Compressive
Strength test in order to assess the strength of AAC blocks. The current project intends to analyse the physical and mechanical
properties of autoclaved aerated concrete blocks at three different curing conditions using an accelerated curing tank to compare
the effects of curing on the properties of AAC.
Keywords: Aerated Concrete, Foam Concrete Pozzolanic Materials, Filler Materials, Compressive Strength

I. INTRODUCTION
One of the most important directions in modern building material science is the development and introduction of new effective heat-
insulating materials, which is mainly due to the growth of the electricity rate and the cost of energy needed for heating buildings.
As for the energy efficiency of buildings, increasingly stringent requirements for the thermal resistance of enclosing structures and
controlled environment improvements in buildings are worth mentioning [1]. Lightweight concrete with a low density is an example
of a material with efficient thermal characteristics and sound insulation for the structure. Lightweight materials can enhance the
seizure capability of a building. The following are the different types of lightweight concrete: (a) Lightweight Aggregate Concrete;
(b) Aerated, Cellular, Foamed, or Gas Concrete, which can be manufactured by creating bubble voids within the concrete or mortar
mass using suitable air-entraining agents and provides greater homogeneity and distribution of the voids within the concrete; and (c)
No-Fines Concrete, which can be manufactured by removing the fine aggregates from the mix, resulting in no segregation of the
fine. It can be classified as (a) Structural Lightweight Concrete, (b) Masonry Concrete, or (c) Both shown in Figure.1 [2]. The
Thermal Coefficient of the insulating concrete should be less than approximately 0.3 J/m2 s °C/m.Different types of pozzolanic
materials can be used as a replacement for the binder in concrete to reduce CO2 emissions caused by OPC. GGBFS, fly ash, and
silica have been used in place of OPC and were accounted to achieve better physical properties. In the presence of moisture,
pozzolanic materials form calcium silicate hydrates after a chemical reaction withcalcium hydroxide.

Fig.1. Classification of Lightweight AeratedConcrete

©IJRASET: All Rights are Reserved | SJ Impact Factor 7.538 | ISRA Journal Impact Factor 7.894 | 2773
 International Journal for Research in Applied Science & Engineering Technology (IJRASET)
ISSN: 2321-9653; IC Value: 45.98; SJ Impact Factor: 7.538
Volume 11 Issue IV Apr 2023- Available at www.ijraset.com

Sustainable waste can be used to partially replace aggregate in concrete. The accumulation of waste can have a negative impact on
the environment. It can also be viewed as an effective way to recycle waste. Reusing or recovering waste has two main advantages.
It moderates the use of ordinary resources and protects the use of landfills for non- reusable materials. Certain pre-treatment methods
can be applied to improve the bond between the concrete matrix and the waste. Thus, an increase in strength was observed with the
addition of the surface-modified waste. Concrete mixed with cement and pozzolanic materials are stronger than concrete mixed with
cement alone. Concrete containing silica fume was tested with different proportions of rubber granules. The combination of crumb
rubber and silica fume is stronger than the combination of crumb rubber and cement [3].

A. Aerated Concrete
Aerated Concrete is a new lightweight, highly insulating and durable building material available in a variety of sizes and thicknesses.
Compared to red brick, aerated concrete blocks are lightweight. Aerated concrete blocks are two to three times lighter than regular
concrete blocks. Aerated concrete can be divided into two grades based on the curing process. Autoclaved Aerated Concrete (AAC)
and Non-Autoclaved Aerated Concrete (NAAC) [4]. Several studies have been conducted to investigate the effects of mixing ratio,
thermal inertia properties, water-to-solid ratio, vapor pressure, and curing time on the properties of Autoclaved Cellular Concrete
[5]. The amount of aluminium powder added affects the density of aerated concrete. Aluminium powder is the most commonly used
air entrainment material. Hydrogen peroxide, bleaching powder, and calcium carbide can also be used, but release hydrogen,
oxygen, and acetylene accordingly [6]. To obtain accurate physical properties of concrete, the porosity of AAC must be determined.
Hydration reactions can be enhanced by high-pressure steam conditions. High-pressure steam also improves the properties of
concrete. Microstructural studies of AAC show that hydration products fill the pores of concrete [7]. AAC blocks are approximately
85% lighter than red bricks, which can reduce structural weight. In other words, AAC blocks are inexpensive and have reasonable
compressive strength [8].
AAC density is reduced by fly ash and GGBFS [16]. GGBFS initiates pozzolanic reactions to form CSH gels when mixed with
cement. This makes GGBFS a suitable partial replacement for cement. In GGBFS, a pozzolanic reaction occurs after a certain age.
Compressive strength values increase as the amount of GGBFS increases to 30% [9]. Replacing cement with GGBFS and fly ash
helps aerated concrete reaches a strength of 25 MPa. Studies have been carried out on aerated concrete with various fillers. Rubber
dust can also be used as a filler in aerated concrete. The exchange gives a less dense mixture. The optimal dosage of rubber powder
was found to be 5% [3]. The addition of fillers also affects the workability of concrete. Induction furnace slag can be used as a semi-
substitute for fines. However, workability shows a decrease in concrete with over 40% replacement of fine aggregate due to its
angular nature [10]. Workability also depends on the addition of various mineral admixtures. Workability increases initially with the
addition of mineral admixtures but decreases with higher cement replacement rates [11]. Superplasticizer dosage should be
optimized based on admixture- cement compatibility and admixture-admixture compatibility. The workability of concrete is reduced
by the addition of a liquefier [12].
Recently, a study was organized investigating the use of quarry dust as a substitute for natural aggregates. Experiments are
conducted using conventional concrete pouring methods. Quarry dust, which is generated in large quantities both onsite and offsite,
is a by-product of stone cutting, grinding, screening, and crushing and poses several environmental concerns. This reduces energy
consumption and greenhouse gas emissions. About 30% of the total stone waste comes from quarries. This vast amount ends up in
landfills [10]. A trade publication has investigated the use of waste as filler in aerated concrete, which is harmful to the environment
and human well-being. Replacing granite powder has a positive effect on workability, strength and durability. Marble powder fills
the pores created by aluminium powder and increases the strength of aerated concrete. Energy efficiency is improved by using
rubber and rubber products instead of fly ash. In this way, the use of waste reduces disposal costs and land area [13]. A better
concept is to incorporate the benefits of lightweight concrete into the fabrication of masonry structures. The production of concrete
for casting masonry blocks is different from the different types of concrete for lightweight building blocks. To reduce costs and
shrinkage, less cement should be used [14]. Conventional concrete blocks are typically cast with very little water and minimal slump.

B. Foam Concrete
Foamed concrete is produced either by the pre- foaming method or mixed foaming method Pre-foaming method involves the
separate production of??base??mix??cement, slurry (cement paste or mortar) and a stabilized aqueous (water-based foam agent),
and then the thorough blending of foam into a base mix [18]. In mixed foaming, the surface-active agent is mixed with the base
mixture. During the process of mixing, the addition of ingredients helps to form a foam-producing cellular structures in concrete as
shown in Fig. 2.

©IJRASET: All Rights are Reserved | SJ Impact Factor 7.538 | ISRA Journal Impact Factor 7.894 | 2774
 International Journal for Research in Applied Science & Engineering Technology (IJRASET)
ISSN: 2321-9653; IC Value: 45.98; SJ Impact Factor: 7.538
Volume 11 Issue IV Apr 2023- Available at www.ijraset.com

Fig. 2. Classification of Foamed Concrete

The preformed foam can be either wet or dry. The wet foam is produced by spraying a solution of the foaming agent over a fine
mesh, has a bubble size of 2 to 5 mm, and is relatively less stable. Dry foam is produced by forcing the foaming agent solution
through a series of high-density restrictions and forcing compressed air simultaneously into the mixing chamber. Foaming agents
are used to obtain foamed concrete. It's called an air entrainer [19]. Foaming agents have the greatest impact on foamed concrete.
When blowing agents are added to the mixing water, they create individual bubble cavities that are incorporated into the cement
paste. The properties of foam concrete are highly dependent on the quality of the foam. Air voids are limited from 10% to 70% in
aerated concrete created by air pockets. These air pockets can be generated by protein or synthetic-based propellants. Various
methods can be used to create these air pockets [20]. A volume fraction of preformed foam can be incorporated into the cement
paste by a method known as the physical foaming process. Air entrainment agents such as H2O2, fine aluminium or zinc powder
can be used to entrain air into the cement paste through a chemical reaction. This process is known as Chemical Aeration
Technology [21]. These two materials have different air entrainment mechanisms. Protein-based foam concentrates generate air
bubbles through protein breakdown. They generate stable gas bubbles through the formation of hydrogen bonds between molecular
groups [21,22]. Synthetic builders are hydrophilic, so they dissolve easily in water and generate air bubbles. Drainage, coalescence,
and disproportional can affect foam stability. Therefore, different blowing agents produce foamed concrete with different
performance [20]. The type of blowing agent used has a significant effect on the fluidity, compressive strength, water absorption,
drying shrinkage and frost resistance of freshly foamed concrete [23,31]. It also affects the thermal resistance and adsorption
coefficient of foam concrete [24].
Supplementary Cementitious Materials (SCMs) are the by-product of industrial production processes which can be used to improve
the strength and durability of foam concrete due to its pozzolanic action. Silica fume, metakaolin, fly ash, and GGBFS are some of
the important SCMs. These SCMs can be used either individually or as a partial replacement for cement [26]. Even though they do not
contribute much to the early strength development, considerable increase in later strength is obtained considering the effect of filler
type (fly ash) on foam concrete. A locally available foaming agent, 53-grade Portland cement, coarse river sand and class F fly ash
were used for the experiment. Mixes which were prepared with fly ash as filler showed a better consistency value, increased strength due to
increase in fineness, higher flow characteristics and an improved strength-to-density ratio [28,32]. However, with rise in density,
water absorption decreased Very few studies have been made by incorporating GGBFS in foam concrete. GGBFS is
a by-product of iron manufacturing which when added to concrete enhances its properties like workability, strength and durability
[29,30].

©IJRASET: All Rights are Reserved | SJ Impact Factor 7.538 | ISRA Journal Impact Factor 7.894 | 2775
 International Journal for Research in Applied Science & Engineering Technology (IJRASET)
ISSN: 2321-9653; IC Value: 45.98; SJ Impact Factor: 7.538
Volume 11 Issue IV Apr 2023- Available at www.ijraset.com

II. PRODUCTION OF AUTOCLAVED AERATED CONCRETE

Fig. 3. Process Phases of AAC Production

A mixture of finely ground sand, cement, quicklime (quicklime), anhydrite or gypsum, and aluminium powder or paste
(foaming agent) is mixed with water to form a slurry [6]. The slurry is then poured into steel moulds to about two-thirds the volume
of the mould. A reaction then takes place between aluminium and water in an alkaline environment to produce hydrogen gas (H2).
Small air bubbles are generated and as the slurry hardens, the expanding air bubbles create a cake-like product that fills the volume of
the mould. In the manufacture of reinforcing elements such as floor, wall and roof panels, corrosion-resistant steel reinforcements
are placed in the mould either before or immediately after the casting.
During the so-called rising process, the cake generates heat due to the dissipative reaction of the burned lime. This accelerates the
hardening reaction of the cement and the "cake" develops sufficient green strength for handling after about 2-4 hours. The cake is
then cut horizontally and vertically into blocks or slabs using cutting equipment such as high-pressure wires and forming knives.
The cut cake is then transferred to an autoclave where hot saturated steam initiates the curing process of the AAC material. The
typical pressure range is 1.1-1.3MPa (160-190 psi) and temperature range is 190-205°C (380-400°F).
In the hardening process, finely ground sand reacts with lime and water to form a specific hydrated calcium silicate crystal
structure known as tobermorite (C5S6H5). This is a natural mineral. After about 12 hours the finished building material is ready for
packing, shipping and assembly. The material hardensfurther after autoclaving process [7,18].

III. CHARACTERISTICS OF AERATED CONCRETE

A. Workability
Workability is measured using a flow chart. The workability of cement paste or mortar is based on fluidity. Flowability or
processability increases as the ratio of water to solids increases. Hard-paste is not suitable for the production of aerated concrete
[33].

B. Density
The water-to-cement ratio is a factor that affects the aeration rate and thus the density of the concrete. If made of pozzolanic
material, consider the water-to-solids ratio, not the water- to-cement ratio. The water-to-cement ratio should not be too low due to
poor aeration and should not be too high due to cavity eruption. Therefore, the water-cement ratio is assumed based on the
consistency of concrete and there is no point in choosing a given one.

C. Water Absorption
As the density of concrete increases, the water absorption decreases. According to the water absorption at constant density
decreased with increasing curing temperature. The comparative density of with the lowest water absorption is at a temperature of 90
°C [34].

©IJRASET: All Rights are Reserved | SJ Impact Factor 7.538 | ISRA Journal Impact Factor 7.894 | 2776
 International Journal for Research in Applied Science & Engineering Technology (IJRASET)
ISSN: 2321-9653; IC Value: 45.98; SJ Impact Factor: 7.538
Volume 11 Issue IV Apr 2023- Available at www.ijraset.com

D. Micro Structure
Micro structural properties of the aerated concrete is the concrete in which large number of voids are uniformly distributed to
reduce the density. This study reports the investigations conducted on the structure of cement-based autoclaved aerated concrete
(AAC) and non- AAC with sand or fly ash as the filler. The variation of the compressive strength, flexural strength etc. are explained
based on the micro structure and the analysis was based on SEM and XRD. Micro structure of the aerated concrete may be altered
due to the curing conditions, compositional variation of filler materials etc. The hydration process in the cement based autoclaved
aerated concrete will be faster than the aerated concrete containing sand and fly ash as filler. Because, the fly ash will be surrounded
by the hydration products formed by cement and slow down the hydration process. The rate of hydration also affects the micro
structure. So that, the micro structure of cement based AAC will be stable with time. The reaction products in the AAC will be
better crystalline and in non-AAC, it will be poorly crystalline. So, AAC possesses good strength compared to others. An inter-
transition zone is present at the void-paste interface. The voids act as aggregates of zero density. The transition zone will be less
porous and unlimited space is available for hydration and move out the bleed water [6].

IV. CONCLUSIONS
Aerated lightweight concrete is unlike conventional concrete in some of its materials and properties. Aerated lightweight concrete
does not contain coarse aggregate and has many advantages, including low density with higher strength when compared to
conventional concrete, improved thermal and sound insulation, and reduced dead load, which could result from several advantages,
such as decreased structural elements and reduced transferred the load to the foundations and bearing capacity. Foamed concrete is
different at the end of the process of forming air voids as compared with autoclaved aerated concrete. The air voids in foamed
concrete are formed by foam agents; this operation is physical processing. The air voids in autoclaved aerated concrete are formed
by adding the aluminium powder to the other materials and the action between them; this operation is chemical processing. The air
voids are homogenously distributed within aerated lightweight concrete. The compressive strength of foamed concrete can be
developed to reach structural strength compared with autoclaved aerated concrete. Aerated lightweight concrete is considered the
most economical in terms of materials,consumption by-products, and waste materials such as fly ash and GGBS.

REFERENCES
[??] Wenyi Hu, Ronald D. Neufeld; Luis E. Vallejo; “Strength Properties Of Autoclaved Cellular Concrete With High Volume Fly Ash” ASCE.August, 1997.
[2] Experimental Study of High-Performance Autoclaved Aerated Concrete Produced with Recycled Wood Fibre and Rubber Powder.” He, Tingshu, Rongsheng,
et al. (2019), Journal of Cleaner Production 234: 559–67.
[3] Experimental Investigation of Autoclaved Aerated Concrete. Avadhoot Bhosale1 ; Nikhil P. Zade2 ; Robin Davis3. DOI: 10.1061/(ASCE)MT.1943-
5533.0002762. © 2019 American Society of Civil Engineers.
[4] “Mechanical properties and development of lightweight concrete by using autoclaved aerated concrete (AAC) with aluminium powder.” Materials Today:
Proceedings 56(2022) 3734–3739 Abhishek Thakur and Saurav Kumar. (2022):
[5] “Structure and properties of aerated concrete: a review”. Cement & Concrete Composites 22 (2000): 321-329. N. Narayanan, K. Ramamurthy. (2000),
[6] New Masonry Product for the US Designer Emerges – Autoclaved Aerated Concrete. John H. Matthys, Ph. D. 2018 American Society of Civil Engineers
[7] Reaction Behavior of Autoclaved Aerated Concrete and Sodium Aluminate at Mild Alkaline and Acid Hydrothermal Conditions: Model for AAC Recycling.
10.1061/(ASCE)MT.1943-5533.0000392. © 2012 American Society of Civil Engineers.
[8] Thermal Inertia?? Properties of Autoclaved Aerate Concrete. by Lawrence Ropelewski1 And Ronald D. Neufeld,2 Member, Asce Vol. 125, No.
2,August,1999. q Asce
[??] Sustainable Usage of Waste Materials in Aerated and Foam Concrete, Indu Susan Raj, Karthiyaini Somasundaram*Civil Engineering and Architecture 9(4):
1144-1155, 2021 http://www.hrpub.org.DOI: 10.13189/cea.2021.090416
[10] Analysis of Microstructure and Properties of Autoclaved Aerated Concrete Wall Construction Materials J. Ind. Eng. Kyo-Seon Kimchi., Vol. 13, No. 7,
(2007) 1103-1108
[11] Study on the Properties of Aerated Cement Paste Incorporating Fly Ash and PVC Granules, National Conference on Recent Emerging
Advances In Civil Engineering And Technology, Tom Damion, Dr. Elson John and Indu Susan Raj, April 2018
[12] Preparation and properties of autoclaved aerated concrete using coal gangue and iron ore tailing, Chang-long Wang, Eni, Construction and Building materials
104(2016) 109-155
[13] An Experimental study on cyclic behaviour of aerated concrete block masonary walls retrofitted with different methods,Mehmet Emin Arslan,elesver (2019).
[14] Evaluation of Exterior Wall Behavior Using Reinforced Autoclaved Aerated Concrete as Cladding, Shane Wilson1 ; Caleb Jennings,
10.1061/(ASCE)ST.1943-541X.0002221. ©2018 American Society of Civil Engineers.
[15] Study on Aerated Concrete Blocks,Athira M, Indu Susan Raj, Dr. Elson John,Iso 9001:2008 Certified Journal.
[????] Development of Autoclaved Aerated Concrete from Mechanically Activated Magnesium-Rich Nickel Slag.DOI;10.1061/(ASCE)@ 2018 American Society
of Civil Engineering.
[????] Preparation and characterization of foamed concrete using a foaming agent and local mineral resources from, Burkina Faso,March 2023, 100365
[????] Materials, Production, Properties and Application of Aerated Lightweight Concrete, Civil Engineering Vol. 2, No. 2 December 2014

©IJRASET: All Rights are Reserved | SJ Impact Factor 7.538 | ISRA Journal Impact Factor 7.894 | 2777
 International Journal for Research in Applied Science & Engineering Technology (IJRASET)
ISSN: 2321-9653; IC Value: 45.98; SJ Impact Factor: 7.538
Volume 11 Issue IV Apr 2023- Available at www.ijraset.com

[????] Comparative study on the performance of protein and synthetic-based foaming agents used in foamed concrete, Volume 14, June 2021, e00524,
https://doi.org/10.1016/j.cscm.2021.e00524
[??] Investigation of the effect of silica fume and synthetic foam additive on cell structure in ultra-low density foam concrete, Burçin S ̧ enol S ̧ Eker, Volume
14, June 2021, e00524,
[????] Improving the compressive performance of foam concrete with ceramsite: Experimental and meso-scale numerical investigation, XiaojuanWang,LuLiu,
Volume 208, October 2021, 109938
[????] Experimental Study On Foam Concrete, Maheshkumar H. Thakrele, Issn(P): 2249-6866; Issn(E): 2249-7978
[????] Physical and mechanical properties of expanded vermiculite (EV) embedded foam concrete subjected to elevated temperatures Jingbo Liu a Yan,Zhuge a,
Volume 16, June 2022, e01038
[????] The influence of superplasticiser on mechanical, transport and microstructure properties of foam concrete, AbdullahAl-ShwaiterHanizamAwang, February
2021
[????] Properties and modification of sustainable foam concrete including eco-friendly recycled powder from concrete waste, DingyiYang, Volume 16, June 2022,
e00826
[????] Influence of self-ignition coal gangue on properties of foam concrete with steam curing, Volume 17, December 2022, e01316
[????] Foamed concrete containing fly ash: Properties and application, to backfilling, Yong-gui Chen a, Lei-lei Guan, Volume 16, June 2022, e01038
[????] Experiments on Foamed Concrete for the Development of Building Blocks Sajan K Jose, Mini Soman, Sheela Evangeline Y, ISSN: 2277-3878, Volume-8
Issue-5, January 2020
[????] Experimental investigation on the compressive strength of foamed concrete: Effect of curing conditions, cement type, foaming agent and dry densityDevid
Falliano , Dario De Domenico a, Giuseppe Ricciardi a, Ernesto Gugliandolo, Volume 16, June 2022, e01038
[??] Evaluation of fresh cement pastes containing quarry by-product powders Rudiele Aparecida Schankoski a,⇑ , Ronaldo Pilar a, Luiz Roberto Prudêncio Jr. a,
Raissa Douglas Ferron b
[????] Jay G. Sanjayan, Ali Nazari , Lei Chen, Giang Hoang Nguyen (2015) Physical and mechanical properties of lightweight aerated geopolymer” Construction and
Building Materials,79,236–244
[????] E. Muthu Kumar, K. Ramamurthy (2017)“Influence of production on the strength, density and water absorption of aerated geopolymer paste and mortar using
Class F fly ash”, Construction and Building Materials, 156 , 1137–1149
[????] Introduction to Architectural Aspects and Developments in Research on Structural Performance of Autoclaved Aerated Concrete ?? (AAC) Products,
DOI:10.1061/40699(2003)46, Architectural Engineering Conference (AEI) 2003

©IJRASET: All Rights are Reserved | SJ Impact Factor 7.538 | ISRA Journal Impact Factor 7.894 | 2778