    Pull Off Test Report Refinary

    Uploaded by

    Zaid Raslan Ayoub
    The document summarizes a pull-off test report for a coating system applied at the Jordan Petroleum Refinery by Al asreyah. Testing was conducted over two days in accordance with ASTM D 4541 and ISO 4624 standards using an Elcometer 108 device. Test results showed pull-off strengths ranging from 2.67 to 8 MPa across 5 test locations, with varying levels of cohesive fractures observed in the primer layers. The report was prepared by SAMARA Training & Development and reviewed by JBC.

    Copyright:

    © All Rights Reserved
    Download as DOCX, PDF, TXT or read online from Scribd

    Pull Off Test Report Refinary

    Uploaded by

    Zaid Raslan Ayoub
    130 views3 pages
    The document summarizes a pull-off test report for a coating system applied at the Jordan Petroleum Refinery by Al asreyah. Testing was conducted over two days in accordance with ASTM D 4541 and ISO 4624 standards using an Elcometer 108 device. Test results showed pull-off strengths ranging from 2.67 to 8 MPa across 5 test locations, with varying levels of cohesive fractures observed in the primer layers. The report was prepared by SAMARA Training & Development and reviewed by JBC.

    Original Title

    Pull off test report refinary

    Copyright

    © © All Rights Reserved

    Available Formats

    DOCX, PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    The document summarizes a pull-off test report for a coating system applied at the Jordan Petroleum Refinery by Al asreyah. Testing was conducted over two days in accordance with ASTM D 4541 and ISO 4624 standards using an Elcometer 108 device. Test results showed pull-off strengths ranging from 2.67 to 8 MPa across 5 test locations, with varying levels of cohesive fractures observed in the primer layers. The report was prepared by SAMARA Training & Development and reviewed by JBC.

    Copyright:

    © All Rights Reserved
    Download as DOCX, PDF, TXT or read online from Scribd
    Download as docx, pdf, or txt
    130 views3 pages

    Pull Off Test Report Refinary

    Uploaded by

    Zaid Raslan Ayoub
    The document summarizes a pull-off test report for a coating system applied at the Jordan Petroleum Refinery by Al asreyah. Testing was conducted over two days in accordance with ASTM D 4541 and ISO 4624 standards using an Elcometer 108 device. Test results showed pull-off strengths ranging from 2.67 to 8 MPa across 5 test locations, with varying levels of cohesive fractures observed in the primer layers. The report was prepared by SAMARA Training & Development and reviewed by JBC.

    Copyright:

    © All Rights Reserved
    Download as DOCX, PDF, TXT or read online from Scribd
    Download as docx, pdf, or txt
    of 3

    T (962)796 686 186

    T (962)799 613 893


    F (962) 6 563 90 38
    E [email protected]
    W www.stdjo.com

    Pull off test Report


    Project:
    Owner: Jordan petroleum refinery
    Paint Applicator: Al asreyah
    Device used Elcometer 108
    Reference ASTM D 4541 & ISO 4624
    Type of adhesive used: Gorilla Glue
    Curing time for abrasive 1 Hour
    Dolly Diameter 20 mm
    Date of Inspection 06-April-2022 to 07-April-2022

    Scope
    Conducting pull – off test to evaluate the adhesion of existing applied coating system

    References
     ASTM D 4541: Standard test method for pull-off strength of coating using portable
    adhesion tester.
     ISO 4624: paint and varnishes – pull-off test for adhesion

    Test result

    Area Pull-Off Type of Failure Description of


    Strength Failure
    Cohesive
    Location No.1
    6 Mpa 100% (B) fracture in
    (dolly No.1)
    primer
    10% cohesive
    fracture in
    primer coat and
    Location No.2
    2.67 Mpa 10% (B), 90% (B/C) 90 % adhesive
    (dolly No.2)
    fracture in
    primer and final
    coat
    Cohesive
    Location No.3
    5.38 Mpa 100% (B) fracture in
    (dolly No.3)
    primer
    Cohesive
    Location No.4
    8 Mpa 100% (B) fracture in
    (dolly No.4)
    primer
    Location No.5 6.62 Mpa 100% (B) Cohesive
    T (962)796 686 186
    T (962)799 613 893
    F (962) 6 563 90 38
    E [email protected]
    W www.stdjo.com

    fracture in
    (dolly No.5)
    primer
    *The pull off test was carried out with Elcometer108 in accordance with ASTM D 4541 and ISO
    4624
    T (962)796 686 186
    T (962)799 613 893
    F (962) 6 563 90 38
    E [email protected]
    W www.stdjo.com

    ISSUED BY SAMARA Training & Development JBC


    Prepared By Reviewed By
    Signature

    Name
    Title
    Date

    You might also like