    Typical Properties: Mil Marketing International Ltda. - Representante en Chile de Jyoti Ceramic Industries LTD

    Uploaded by

    Felipe Reyes Gallardo
    This document provides typical properties of two ceramic coating products from Jyoti Ceramic Industries Ltd: Aluma Coat-TW (trowelable) and Aluma Coat-BR (brushable). It lists specifications for each including type, color, appearance, particle size, mixing ratio, pot life, curing time, application method, coverage rate, service temperature, and mechanical strengths like compressive strength and hardness. Both provide corrosion resistance when tested according to industry standards.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Typical Properties: Mil Marketing International Ltda. - Representante en Chile de Jyoti Ceramic Industries LTD

    Uploaded by

    Felipe Reyes Gallardo
    40 views1 page
    This document provides typical properties of two ceramic coating products from Jyoti Ceramic Industries Ltd: Aluma Coat-TW (trowelable) and Aluma Coat-BR (brushable). It lists specifications for each including type, color, appearance, particle size, mixing ratio, pot life, curing time, application method, coverage rate, service temperature, and mechanical strengths like compressive strength and hardness. Both provide corrosion resistance when tested according to industry standards.

    Original Title

    ALUMA COAT

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides typical properties of two ceramic coating products from Jyoti Ceramic Industries Ltd: Aluma Coat-TW (trowelable) and Aluma Coat-BR (brushable). It lists specifications for each including type, color, appearance, particle size, mixing ratio, pot life, curing time, application method, coverage rate, service temperature, and mechanical strengths like compressive strength and hardness. Both provide corrosion resistance when tested according to industry standards.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    40 views1 page

    Typical Properties: Mil Marketing International Ltda. - Representante en Chile de Jyoti Ceramic Industries LTD

    Uploaded by

    Felipe Reyes Gallardo
    This document provides typical properties of two ceramic coating products from Jyoti Ceramic Industries Ltd: Aluma Coat-TW (trowelable) and Aluma Coat-BR (brushable). It lists specifications for each including type, color, appearance, particle size, mixing ratio, pot life, curing time, application method, coverage rate, service temperature, and mechanical strengths like compressive strength and hardness. Both provide corrosion resistance when tested according to industry standards.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    MIL MARKETING INTERNATIONAL LTDA.

    - REPRESENTANTE EN CHILE DE JYOTI CERAMIC INDUSTRIES LTD

    Typical Properties

    ALUMA COAT – TW ALUMA COAT – BR


    No. PROPERTY
    TROWELLABLE BRUSHABLE

    Two component Epoxy Resin


    based doped with 80-85% Two component Epoxy Resin based doped with
    1. Type
    spherical Alumina Oxide 80% fine sintered ceramic powders.
    Beads

    2. Colour White Terracotta Brown and Grey.

    Granular highly viscous


    3. Appearance at 25°C/77°F Smooth highly viscous paste.
    paste.

    4. Average particle size. 0.4mm - 0.8mm 60 - 65 microns.

    Mixing Ratio

    5. Part I : Part II 100 : 4gms 100 : 8gms

    Epoxy Resin : Hardener by weight by weight

    Pot Life 25°C/77°F for 500


    6. 30 - 45 minutes 30 - 45 minutes
    gms Mix.

    Initial setting time at


    7. 4 - 5 hrs. 4 - 5 hrs.
    25°C/77°F

    24 hrs. for about 5 - 6 mm 24 hrs. for about 0.8 - 1 mm


    8. Curing time at 25°C/77°F

    Thick Coating. Thick Coating.

    9. Application method By Trowel. Brush / Spray

    As per consistency required.

    Thinning recommended by (Approx 5-10% for brush application)


    Thinning with Acetone or
    10. commercially available
    Xylene not recommended.
    Acetone / Xylene.

    For spray application use as per consistency


    required

    Over coat time or time Over coat is not After approx 6-8 Hrs. or when 1st coat has just
    11.
    interval between two coats. recommended. become tack free.

    12. Recommended thickness. About 5 - 6 mm. About 0.8 - 1 mm Thick.

    Approximate coverage per 0.1 m2/Kg. at about 5 mm


    13. 0.7 m2/Kg. at about 0.8 - 1 mm Thick coating.
    Kg. mix. thick coating.

    Maximum service
    14. 150°C / 302°F 150°C / 302°F
    temperature

    15. *Mechanical strengths

    Compressive strength as
    A. 840 Kg./cm2 840 Kg./cm2
    per(ASTM-695 Standards)

    B. Flexural strength (ASTM-790) 700 Kg./cm2 700 Kg./cm2

    C. Adhesive strength. 90 - 95 mpa. 90 - 95 mpa.

    Shore 'D' Hardness (ASTM-D-


    D. 85-90 85-90
    2240)

    Salt / Cyclic corrosion Test.


    According to ASTM B-117-97
    16. standards after 400 Hrs. of No changes observed. No changes observed.
    test at 35°C, PH value 7.2,
    Humidity 95% RH