Sa 285

SPECIFICATION FOR PRESSURE VESSEL PLATES,
CARBON STEEL,
LOW- AND INTERMEDIATE-TENSILE STRENGTH
SA-285/SA-285M
(Identical with ASTM Specification A 285/A 285M-90)
1.
Scope
the other. Combining values from the two systems may

result in nonconformance with the specification.
1.1 This specification covers carbon steel plates of

low- and intermediate-tensile strengths which may be
made by killed, semi-killed, capped, or rimmed steel
practices at the producers option. These plates are
intended for fusion-welded pressure vessels.
2.
2.1 ASTM Standard:

A 20/A 20M Specification for General Requirements for
Steel Plates for Pressure Vessels
1.2 Plates under this specification are available in

three grades having different strength levels as follows:
98
Grade
Tensile Strength,
ksi (MPa)
A
B
C
4565 (310450)
5070 (345485)
5575 (380515)
Applicable Document
3.
General Requirements and Ordering

Information
3.1 Material supplied to this material specification

shall conform to Specification A 20/A 20M. These
requirements outline the testing and retesting methods
and procedures, permissible variations in dimensions
and mass, quality and repair of defects, marking, loading, etc.
1.3 The maximum thickness of plates under this

specification, for reasons of internal soundness, is limited to a maximum thickness of 2 in. (50 mm) for all
grades.
NOTEFor killed carbon steels only refer to the following ASTM
specifications:
3.2 Specification A 20/A 20M also establishes the

rules for the ordering information that should be complied with when purchasing material to this specification.
A 299, Pressure Vessel Plates, Carbon Steel, ManganeseSilicon

A 515 Pressure Vessel Plates, Carbon Steel, for Intermediate and Higher Temperature Service
A 516 Pressure Vessel Plates, Carbon Steel, for Moderate
and Lower Temperature Service
3.3 In addition to the basic requirements of this

specification, certain supplementary requirements are
available when additional control testing or examination
is required to meet end use requirements. The purchaser
is referred to the listed supplementary requirements in
this specification and to the detailed requirements in
Specification A 20/A 20M.
1.4 The values stated in either inch-pound units or

SI units are to be regarded separately as standard.
Within the text, the SI units are shown in brackets. The
values stated in each system are not exact equivalents;
therefore, each system must be used independently of
3.4 If the requirements of this specification are in

conflict with the requirements of Specification A 20/
451
98
SA-285/SA-285M
1998 SECTION II
A 20M, the requirements of this specification shall

prevail.
5.
Chemical Requirements
5.1 The steel shall conform to the requirements as

to chemical composition shown in Table 1.
6.
Mechanical Requirements
6.1 Tension Tests:
4.
Heat Treatment
6.1.1 Requirements:
4.1 Plates are normally supplied in the as-rolled

condition. The plates may be ordered normalized or
stress relieved, or both.
6.1.1.1 The material as represented by the tension-test specimens shall conform to the requirements
shown in Table 2.
TABLE 1
CHEMICAL REQUIREMENTS
98
Composition, %
Elements
max A
Carbon,
Manganese, max
Heat analysis
Product analysis
Phosphorus, max A
Sulfur, max A
A
Grade A
Grade B
Grade C
0.17
0.22
0.28
0.90
0.98
0.035
0.035
0.90
0.98
0.035
0.035
0.90
0.98
0.035
0.035
Applied to both heat and product analysis.
TABLE 2
TENSILE REQUIREMENTS
Grade A
Tensile strength
Yield strength, min A
Elongation in 8 in. or [200 mm], min, % B
Elongation in 2 in. or [50 mm], min, %
A
B
Grade B
ksi
[MPa]
ksi
4565
24
[310450]
[165]
27
30
5070
27
Determined by either the 0.2% offset method or the 0.5% extension-under-load method.
See Specification A 20/A 20M.
452
[MPa]
[345485]
[185]
25
28
Grade C
ksi
[MPa]
5575
30
[380515]
[205]
23
27
98
PART A FERROUS MATERIAL SPECIFICATIONS
SUPPLEMENTARY REQUIREMENTS
Supplementary requirements shall not apply unless specified in the order.
A list of standardized supplementary requirements for use at the option of the
purchaser are included in Specification A 20/A 20M. Those which are considered
suitable for use with this specification are listed below by title.
98
S3.
Simulated Post-Weld Heat Treatment of

Mechanical Test Coupons.
S4.1 Additional Tension Test.

S14. Bend Test.
ADDITIONAL SUPPLEMENTARY REQUIREMENTS

Also listed below are additional optional supplementary requirements suitable for
this specification.
98
S57. Copper-Bearing
S57.1 The copper content, by heat analysis shall be
0.200.35% and by product analysis 0.180.37%.
98
S58. Restricted Copper

S58.1 The maximum incidental copper content by
heat analysis shall not exceed 0.25%.
453
SA-285/SA-285M

Sa 285

Uploaded by

Copyright:

Available Formats

Sa 285

Uploaded by

Document Information

Original Description:

Original Title

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

Sa 285

Uploaded by

Copyright:

Available Formats

SPECIFICATION FOR PRESSURE VESSEL PLATES,

the other. Combining values from the two systems may

1.1 This specification covers carbon steel plates of

2.1 ASTM Standard:

1.2 Plates under this specification are available in

General Requirements and Ordering

3.1 Material supplied to this material specification

1.3 The maximum thickness of plates under this

3.2 Specification A 20/A 20M also establishes the

A 299, Pressure Vessel Plates, Carbon Steel, ManganeseSilicon

3.3 In addition to the basic requirements of this

1.4 The values stated in either inch-pound units or

3.4 If the requirements of this specification are in

A 20M, the requirements of this specification shall

5.1 The steel shall conform to the requirements as

4.1 Plates are normally supplied in the as-rolled

Applied to both heat and product analysis.

PART A FERROUS MATERIAL SPECIFICATIONS

Simulated Post-Weld Heat Treatment of

S4.1 Additional Tension Test.

ADDITIONAL SUPPLEMENTARY REQUIREMENTS

S58. Restricted Copper