TECHNICAL DATA
TENCATE ADVANCED COMPOSITES
MS-4H
PRODUCT TYPE 280F (138C) Fast Cure Standard Modulus Compression Molding System
PRODUCT DESCRIPTION MS-4H is a 1 carbon fiber/epoxy resin compression molding system. This is an excellent low cost, high performance carbon fiber molding compound that has been qualified to military and commercial applications. It has excellent out time stability and processes very well in medium to large heavy parts.
* For very small or thin parts, consideration should be given to the 1/2 fiber length version or to MS-1H-1/2 for better uniformity of fiber distribution.
MS-4H PHYSICAL PROPERTIES SHELF LIFE 6 months at 0F (-18C) Fiber Length.............................................................1 in. Density.....................................................................1.48-1.52 g/cc Thermal Expansion X,Y............................................3-5 ppm/F (5.4-9.0 ppm/C) Tg (by DSC)...............................................................375F (191C) Post Cured at 350F (177C) MS-4H MECHANICAL PROPERTIES.
Properties Tensile Strength 0 Tensile Modulus 0 Compressive Strength 0 Compressive Modulus 0 Flexural Strength 0 Flexural Modulus 0 Open Hole Comp. Strength Compression After Impact Notched Shear Strength Notched Shear Modulus Bolt Bearing Str. (Single Shear) Condition (RTD, ETD, ETW) RTD RTD RTD RTD RTD RTD RTD RTD RTD RTD RTD Method ASTM D3039 ASTM D3039 ASTM D6484 ASTM D6484 ASTM D6272 ASTM D6272 ASTM D6484 ASTM D7137** ASTM D7078 ASTM D7078 ASTM D5961 43.8 ksi 6.2 Msi 47.9 ksi 7.3 Msi 108.8 ksi 9.3 Msi 38.5 ksi 21.2 ksi 25.8 ksi 1.8 Msi 124.5 ksi Results 302.0 MPa 42.7 GPa 330.3 MPa 50.3 GPa 750.2 MPa 64.1 GPa 265.4 MPa 146.2 MPa 177.9 MPa 12.4 GPa 858.4 MPa
- All items are net molded coupons unless noted ** Machine Molded, drop weight impact set forth via ASTM D7136-05. - All properties based on a ber volume of 48-50% - All properties based on the average of a 3 batch qualication. Full details are available upon request. - Actual molding technique and conditions, ber length, and part geometry will affect properties obtained. - Data shown for 1 inch (25.4 mm) length material, properties will generally be lower for inch (12.7 mm) and/or inch (6.35 mm). - Above values derrived after post cure of 350F/177C for 1-2 hours.
PROCESS PARAMETERS * Pre-weigh the desired amount of molding compound. * Pre-heat molding compound in 160F 10F (71C 8C) oven for 10 minutes. Form mold charge to approximately fit cavity. Charge cavity with molding compound. * Cure temperature: 280F-310F (138C-154C). Pinch pressure: 250 psi for 15-30 seconds. Close mold to 2,000 psi, hold for 15-30 minutes depending on the part thickness.
Page 1 of 2 MS-4H_DS_042913
* Post cure at 350F/177C for 1-2 hours for full properties.
TECHNICAL DATA
TENCATE ADVANCED COMPOSITES BMC MOLDING GUIDELINES: 1. Pre-weigh the desired amount of molding compound 2. Pre-heat the molding compound at 160F 10F (71C 5.5C) for 10 minutes 3. Form a mold charge to approximately fit the mold cavity 4. Place the charge in the mold cavity 5. Cure: 280-310F. Pinch pressure 250 psi for 15-30 seconds. Close mold to 2000 psi for 15-30 minutes depending on part thickness. 6. Post cure at 350F/ 177C for 1-2 hours. TROUBLE SHOOTING: BLISTERING OR BUBBLES: Check mold surface temperature Increase molding pressure Check for moisture in the material CRACKS OR STRESS MARKS: Check mold surface temperature Check cure time Clean mold surface and re-apply mold release Check ejection pressure, slow down ejection FLOW MARKS: Close press sooner after charge has been placed in the cavity Increase press closure speed Check mold surface temperature RESIN STARVATION: Check material out-time and staging temperature, Keep charge material covered and in plastic bags Adjust charge weight Clean mold surface and re-apply mold release VOIDS: Check charge set-up, shape and weight Check mold surface temperature Check pre-heat time and temperature Check press closure time Clean mold surface and re-apply mold release THICK PART UNEVEN DISTRIBUTION OF MATERIAL Pre-consolidate thick sections Spread molding compound in measured increments Evaluate if press capacity is large enough for even pressure across part GENERAL NOTES:
Revised 04/2013 All data given is based on representative samples of the materials in question. Since the method and circumstances under which these materials are processed and tested are key to their performance, and TenCate Advanced Composites USA, Inc. has no assurance of how its customers will use the material, the corporation cannot guarantee these properties.
Page 2 of 2 MS-4H_DS_042913
MS-4H
Note that 1, , and material will be slightly different with the longer chop length showing as bulkier then the shorter chop lengths. Generally the material does not brick up (unless exposed to heat or warmth) and is typically free flowing as received once broken free of the packaging. Some centering or clumping is not uncommon, however when cool, the material should crumble out of the packaging. The bulk volume of the uncured uncompressed material is ~5X that of the compressed/ cured part. When pre-heated, a pre-formed charge will shrink maybe 10% if no pressure of any kind is applied other then gravity. It may debulk down 20-30% if pressure is applied, even hand pressure. - The calculated cured density of the material is ~1.483 g/cc or ~92.6 lb/ft3. - A 3 lb bag of 1 material will measure out to a football shape when in a bag of ~12x10x5. - This loosely calculates to a 10 to 1 ratio, however the bagged material is not rectangular in shape. www.tencate.com
www.tencateadvancedcomposites.com www.tencateindustrialcomposites.com E-mail: [email protected] (USA) E-mail: [email protected] (Europe) ISO 9001 Registered AS 9100 2450 Cordelia Road Fairfield, CA 94534 USA Tel: +1 707 359 3400 Fax: +1 707 359 3495
TENCATE ADVANCED COMPOSITES

18410 Butterfield Blvd. Morgan Hill, CA 95037 USA Tel: +1 408 776 0700 Fax: +1 408 776 0107 Campbellweg 30 7443 PV Nijverdal NL Tel: +31 548 633 933 Fax: +31 548 633 299

MS-4H MSDS

Uploaded by

Copyright:

Available Formats

MS-4H MSDS

Uploaded by

Document Information

Original Description:

Copyright

Available Formats

Share this document

Share or Embed Document

Sharing Options

Did you find this document useful?

Is this content inappropriate?

Copyright:

Available Formats

MS-4H MSDS

Uploaded by

Copyright:

Available Formats

TECHNICAL DATA

TENCATE ADVANCED COMPOSITES

* Post cure at 350F/177C for 1-2 hours for full properties.

TENCATE ADVANCED COMPOSITES

You might also like