NORSOK STANDARD

M-123
Edition 2, October 2012

Forged structural steel

This NORSOK standard is developed with broad petroleum industry participation by interested parties in the Norwegian petroleum industry and is owned by the Norwegian petroleum industry represented by The Norwegian Oil Industry Association (and The Federation of Norwegian Industry. Please note that whilst every effort has been made to ensure the accuracy of this NORSOK standard, neither The Norwegian Oil Industry Association nor The Federation of Norwegian Industry or any of their members will assume liability for any use thereof. Standards Norway is responsible for the administration and publication of this NORSOK standard. Standards Norway Strandveien 18, P.O. Box 242 N-1326 Lysaker NORWAY Copyrights reserved Telephone: + 47 67 83 86 00 Fax: + 47 67 83 86 01 Email: [email protected] Website: www.standard.no/petroleum

NORSOK standard M-123 Foreword Introduction 1 2 2.1 2.2 3 3.1 3.2 4 4.1 4.2 4.3 4.4 4.5 5 5.1 5.2 5.3 5.4 6 6.1 6.2 6.3 6.4 6.5 6.6 6.7 7 7.1 7.2 7.3 7.4 8 9 10 11 12 Scope Normative and informative references Normative references Informative references

Rev. 2, October 2012 2 2 3 3 3 3 3 3 3 4 4 4 4 5 5 7 7 7 7 8 9 9 9 9 9 9 10 10 10 10 10 11 12 12 13 13 13 13

Terms, definitions and abbreviations

Terms and definitions Abbreviations Qualification General Basis for qualification of steel forges General requirements Manufacturing Qualification based upon a test program Requirement to forged structural steel Steel making process Forging process Heat treatment Chemical composition Mechanical testing General Test coupons Test sampling Test methods Retesting and criteria for rejection Mechanical properties Summary of mechanical testing Non destructive testing Personnel Critical areas and extent of testing Methods Acceptance criteria Repair Dimensions/tolerances Surface protection Marking Documentation

NORSOK standard

Page 1 of 13

NORSOK standard M-123

Rev. 2, October 2012

Foreword
The NORSOK standards are developed by the Norwegian petroleum industry to ensure adequate safety, value adding and cost effectiveness for petroleum industry developments and operations. Furthermore, NORSOK standards are, as far as possible, intended to replace oil company specifications and serve as references in the authorities regulations. The NORSOK standards are normally based on recognised international standards, adding the provisions deemed necessary to fill the broad needs of the Norwegian petroleum industry. Where relevant, NORSOK standards will be used to provide the Norwegian industry input to the international standardisation process. Subject to development and publication of international standards, the relevant NORSOK standard will be withdrawn. The NORSOK standards are developed according to the consensus principle generally applicable for most standards work and according to established procedures defined in NORSOK A-001. The NORSOK standards are prepared and published with support by The Norwegian Oil Industry Association, The Federation of Norwegian Industry, Norwegian Shipowners Association and The Petroleum Safety Authority Norway. NORSOK standards are administered and published by Standards Norway.

Introduction
This NORSOK standard is based on former company specifications and experience from deliveries and operation.

NORSOK standard

Page 2 of 13

NORSOK standard M-123

Rev. 2, October 2012

Scope

This NORSOK standard defines the requirements for qualification of forges and the technical delivery requirements for forged structural steel components for use in offshore structures where Steel Quality Level I or II is required.

Normative and informative references

The following standards include provisions and guidelines which, through reference in this text, constitute provisions and guidelines of this NORSOK standard. Latest issue of the references shall be used unless otherwise agreed. Other recognized standards may be used provided it can be shown that they meet the requirements of the referenced standards.

2.1

Normative references

ASME V, Article 2, Radiographic Examination ASME V, Article 7, Magnetic Particle Examination ASME VIII, div.1, appendix 6, Methods For Magnetic Particle Examination ASME VIII, div.1, appendix 7, Methods For Radiographic Examination ASTM A388, Standard Practice for Ultrasonic Examination of Heavy Steel Forgings ASTM A508, Standard specification for quenches and tempered vacuum-treated carbon and alloy steel forgings for pressure vessels ASTM E112, Standard Test Method for Determining Average Grain Size ASTM E709, Standard Practices For Magnetic Particle Examination BS 2634-1, Roughness comparison specimens Part 1: Specification for turned, ground, bored, milled, shaped and planed specimens BS 7448, Fracture mechanics toughness tests EN - 473/Nordtest, Qualification of NDE operators ISO 148, Steel Charpy impact test (V-notch) ISO 6892, Metallic material Tensile testing at ambient temperature ISO 9001, Quality management systems - Requirements (ISO 9001:2000) EN 10204, Metallic materials Types of inspection documents EN 10225, Wieldable structural steels for fixed offshore structures Technical delivery conditions

2.2
None

Informative references

3
3.1

Terms, definitions and abbreviations

Terms and definitions

For the purposes of this NORSOK standard, the following terms, definitions and abbreviations apply.

3.1.1 shall verbal form used to indicate requirements strictly to be followed in order to conform to this NORSOK standard and from which no deviation is permitted, unless accepted by all involved parties 3.1.2 should verbal form used to indicate that among several possibilities one is recommended as particularly suitable, without mentioning or excluding others, or that a certain course of action is preferred but not necessarily required 3.1.3 may verbal form used to indicate a course of action permissible within the limits of this NORSOK standard 3.1.4 can verbal form used for statements of possibility and capability, whether material, physical or casual NORSOK standard Page 3 of 13

NORSOK standard M-123

Rev. 2, October 2012

3.2
ACCT ASME ASNT ASTM BS CTOD EN MT NDT PWHT FATT HAZ CTOD RT UT

Abbreviations
ASNT Central Certification Program American Society Mechanical Engineers Standard American Society for Non-destructive Testing American Society for Testing and Materials British Standard crack tip opening displacement European Standard magnetic particle testing non destructive testing post weld heat treatment fracture appearance transition temperatures heat affected zone crack tip opening displacement radiographic testing ultrasonic testing

4
4.1

Qualification
General

The purchaser may accept the forges qualification based on general information described in 4.2-4.4 combined with a verification or audit at the forgemasters premises. However, depending on the criticality and complexity of the forging and the experience of the forge, the purchaser may require the forge to perform a qualification as described in 4.5.

4.2

Basis for qualification of steel forges

documented knowledge and previous experience with the material and the manufacturing; manufacturing facilities and equipment; established manufacturing procedures covering all important manufacturing steps from melting to finished products; manufacturers quality system, which shall fulfil the requirements of ISO 9001 or equivalent; results of representative testing in compliance with this NORSOK standard.

The basis for qualification is as follows:

Prior to qualification, a complete report, with information and results of representative testing as required by this standard shall be available for review.

4.3

General requirements

The manufacturer shall have knowledge of relevant metallurgical aspects of the applicable steel grades including welding, heat treatment parameters, etc. as applicable for his manufacturing process. The manufacturer shall have knowledge and relevant experience with manufacture of the steel grades to be qualified. Experience should be supported by statistical data or relevant test records for the size range to be qualified. The steel shall have been produced to manufacturing procedures and with equipment intended used for the actual manufacturing. Facilities and equipment shall be fit for purpose, regularly maintained and calibrated as required. The assessment shall concentrate on facilities and equipment for melting, forging, heat treatment, etc. If parts of the production are carried out at a sub-supplier, the manufacturer is responsible for ensuring that the sub-supplier meets the requirements of this Norsok standard for the manufacturing steps that he is performing.

NORSOK standard

Page 4 of 13

NORSOK standard M-123

Rev. 2, October 2012

4.4

Manufacturing

The manufacturer shall have a manufacturing summary for each production route. The Manufacturing Summary shall describe, step by step in a logical and correct sequence all important manufacturing activities with reference to detailed procedures. A short description and the main parameters for each activity shall be included. The production route shall be illustrated with a flow chart. The scope of the manufacturing summary shall be clearly defined as follows: name and address of manufacturer; grade of material with reference to standard; type and size range of products for which the manufacturing summary applies; identification of the manufacturing process.

The manufacturing summary shall include procedures for melting and refining processes (if subcontracted, relevant information to be provided); forging method; heat treatment, including: loading temperature, heating rate, holding temperature (range) and time; loading of components in furnace; type of furnace(s); max. operating temperature for furnace(s); temperature control and calibration of furnace(s); cooling facilities and max. time from furnace to quenching bath (if relevant); sketch of heat treatment facilities/furnace which also shall show location of pyrometers and/or thermocouples in the furnace. blasting/cleaning equipment, incl. type of grit; NDT and inspection; material testing. Type of tests and time of test sampling.

If the manufacturer has different plants or different production routes for a product, separate documentation is required for each of these. If essential parts of the work are subcontracted, this shall be identified in the documentation. Whenever a change is made in the equipment or procedures, the documentation shall be updated accordingly.

4.5

Qualification based upon a test program

4.5.1 General For critical structural forgings or forgings intended for welding, base material and weldability data shall be required documented according to 4.5.2 to 4.5.8 4.5.2 Qualification of the manufacturing process The manufacturing process as described in the manufacturing summary shall be qualified by testing of actual products to a) demonstrate that the proposed manufacturing route and production parameters results in products meeting specified requirements, b) verify that the proposed production test sampling gives results which are representative of the properties in the actual components which they represent. 4.5.3 Validity of qualification

4.5.3.1 General The qualification shall be repeated if there are changes in the production route, the manufacturing procedures or the specified composition or properties of the products which exceeds the limits given below.

NORSOK standard

Page 5 of 13

NORSOK standard M-123

Rev. 2, October 2012

If production is carried out at different plants/locations, a separate qualification is required for each plant. This applies also for change of subcontractors for essential operations, e.g. forged bar/ingot, quality heat treatment. 4.5.3.2 Thickness limitations The maximum thickness qualified is the thickness of the tested product plus 25 %. The qualified maximum and minimum thickness shall in any case not exceed the limits specified in the Manufacturing Summary. 4.5.3.3 Material grade A change from one steel grade to a higher grade (see Table 1) shall require requalification. 4.5.3.4 Type of melting and refining equipment A change of the melting/refining process requires a requalification. 4.5.3.5 Manufacturing equipment A major change of manufacturing equipment requires requalification, unless the new equipment can be regarded as comparable to the old one with respect to its influence on the product properties. This applies also if the manufacturer has several alternative manufacturing routes for a product. 4.5.3.6 Heat treatment A change of heat treatment method, (e.g. a change from normalising and tempering to quenching and tempering) will require requalification. 4.5.4 Selection of material for testing Selection of components for testing and positioning of test samples shall be as agreed between purchaser and the manufacturer. Generally shall both longitudinal and transversal direction compared with the main grain flow, be tested for mechanical properties. 4.5.5 Extent of testing Testing for qualification shall comprise: production testing with test sampling as specified in this Norsok standard. additional testing for qualification as required in this NORSOK standard non-destructive testing as specified in this NORSOK standard. 4.5.6 Base material

4.5.6.1 General The material used for the examinations to document properties shall be representative, implying that the chemical composition and mechanical properties shall be within the guaranteed limits; the steel making process, forging methods and heat treatment condition shall be equal to that proposed for the actual delivery; the reduction ratio shall match the minimum specified ratio, see 5.2.

The tested section thickness shall be representative for the thinnest and thickest portion in the forging for the actual delivery. 4.5.6.2 Chemical composition and mechanical properties The chemical composition and mechanical properties shall be as per Clause 5 and Clause 6.

NORSOK standard

Page 6 of 13

NORSOK standard M-123

Rev. 2, October 2012

4.5.6.3 Charpy V-notch impact test transition curves Charpy V-notch impact test transition curves (-80 C, -60 C, -40 C and 20 C) shall be made for the thickest material section both in longitudinal and transversal/tangential directions. The specimen shall be taken from 2 mm below surface and mid-thickness position. Three specimens shall be tested at each test condition. Both the energy absorption (J) and the), defined as 50 % crystallinity, shall be reported. 4.5.6.4 Micrographic examinations The base material microstructure shall be documented by micrographs of magnification 500X from subsurface, 1/4 thickness and thickness positions. The type of microstructure, grain size and inclusion level shall be reported to satisfy the requirement in 5.2. Testing to be carried out according to ASTM E112. 4.5.6.5 Weldability Weldability data are required for forgings with a weld bevel thickness above 25 mm. The thickness to be used for the weldability test shall be agreed, but is not to be more than 10 % below the weld bevel thickness to be delivered. The documentation of the weldability shall be in accordance with EN 10225, Annex E. The heat input shall be 3,5 0,2 kJ/mm (EN 10225, Table E.3). For weld bevel thicknesses above 50 mm the testing shall be carried out both in the as welded and PWHT condition. CTOD testing is required for weld bevel thickness above 50 mm and shall meet a requirement of minimum 0,25 mm (as-welded) and 0,20 mm (PWHT), at 10 C unless a lower value has been accepted by the purchaser. CTOD testing is limited to only grain-coarsened HAZ. 4.5.6.6 Qualification test record The manufacturer shall present a qualification test record containing results of all required tests as well as details about test sampling and test procedures.

5
5.1

Requirement to forged structural steel

Steel making process

The steel for structural forged components shall be made by the basic oxygen or electric arc furnace process. The steel shall be made with low impurity level and low content of N, O and H, and be free from dangerous cracks, gross laminations, inclusions, segregations, shrinkage and porosity. The steel shall be fully killed and supplied to fine grain practice. The steel shall normally be ingot cast and the filling is to be by bottom feeding. Significantly segregated core and any piped ingot part shall be discarded prior to forging.

5.2

Forging process

The forging shall be mechanically hot worked throughout the section and length and to a shape as close as possible to the final. The working may be pressing, hammering, ring rolling or combination thereof, and where the method shall be selected to give a favourable grain flow and texture for the intended component and application. Care shall be taken to assure that segregated parts of the steel will not be exposed after final machining. The reduction ratio shall be minimum 4:1 for Area 1 and min. 3:1 for Area 2 in order to obtain a minimum grain size of 7 at any section for Area 1 and to a minimum grain size of 5 for Area 2 according to ASTM E112. For area definition, see 7.2.1.

5.3

Heat treatment

5.3.1 General All forgings shall be supplied in one of the following heat treatment conditions: normalised; normalised and stress-relieved; austenitised, quenched and tempered. For stress relieving the temperature shall be in the range of 550 C to 600 C. NORSOK standard Page 7 of 13

NORSOK standard M-123

Rev. 2, October 2012

Heat treatment shall be carried out in properly constructed furnaces, which are efficiently maintained, and have adequate calibrated means for control and recording of temperature. The furnace dimensions shall be such as to allow for the whole forging to be uniformly heated to the specified temperature. Heat treatment records shall be submitted upon request from the purchaser. The heat treatment furnaces shall be calibrated according to ASTM A991 or ISO 10423 Annex M. If, after final heat treatment, a forging is locally re-heated, or any straightening operation giving more than 5 % cold deformation, a repeated final heat treatment has to be conducted.

5.4

Chemical composition

Proposed chemical compositions are given in Table 1. The values apply to both ladle and product analysis. Any modification from Table 1 shall be agreed in each case. - Ladle analysis shall be determined for each ladle - Product analysis shall be determined for each ingot Table 1 Chemical composition Element\Grade C Mn Si S P Cu Ni Cr Mo V a) Nb a) Ti Al tot. N Sb Pb Sn As Bi B max. max. max. max. max. max. min. max. max. max. max. max. max. max. max. max. max. max. max. max. max. 355 ladle/product 0,12 1.65 0,35 0,005 0,015 0,30 0,35 0,70 0,20 0,08 0,050 0,030 0,020 0,040 0,010 0,010 0,005 0,015 0,020 0,005 0,0005 420 ladle/product 0,14 1,65 0,35 0,007 0,015 0,30 0,35 0,70 0,20 0,25 0,050 0,030 0,020 0,040 0,010 0,010 0,005 0,015 0,020 0,005 0,0005 460 ladle/product 0,12 1,60 0,35 0,007 0,015 0,30 0,8 2,8 0,95 0,50 0,050 0,030 0,020 0,040 0,010 0,010 0,005 0,015 0,020 0,005 0,0005 500 ladle/product 0,12 1,60 0,35 0,007 0,015 0,30 0,8 2,8 0,95 0,50 0,050 0,030 0,020 0,040 0,010 0,010 0,005 0,015 0,020 0,005 0,0005 0,55 0,27

CEV max. 0,45 0,47 0,55 Pcm max. 0,22 0,23 0,27 All values are maximum values unless a range is given, all in weight percent.

CEV C Pcm C
a)

Mn Cr Mo V Cu Ni 6 5 15 Si Mn Cu Cr Ni Mo V 5B 30 20 60 15 10

Nb V 0,06%

NORSOK standard

Page 8 of 13

NORSOK standard M-123

Rev. 2, October 2012

6
6.1

Mechanical testing
General

Testing for mechanical properties as yield strength, ultimate tensile strength, elongation, reduction of area and charpy impact energy shall be performed for each forging above 1 ton weight. For smaller forgings, another test frequency may be agreed upon. The results obtained shall comply with the requirement given in Table 2. One set of testing shall be carried out for each heat and treatment load.

6.2

Test coupons

Each forging to be tested shall have full section prolongations for test coupons to represent the thinnest and thickest sections. The test coupons shall not be removed from the forgings until all quality heat treatments have been carried out.

6.3

Test sampling

Unless otherwise agreed, the longitudinal axis and mid-length of test pieces shall be positioned as described below and Table 3: - T< 50 mm: for thickness, t, up to and including 50 mm, the axis shall be at the t/2 and with the midlength of the test piece at least 50 mm from the end - T > 50 mm: for thickness greater than 50 mm, the axis shall be at t/3 or 80 mm, whichever is less, and at sub surface, and with mid-length of the test piece at least 50 mm from the end. Transverse and longitudinal tests shall be made except that rings, hollow forgings which are expanded, and disks shall be tested in tangential and longitudinal direction if length enough for longitudinal testing. For each position and orientation described, a set of tests comprise 1 tensile test and 3 charpy V-notch test specimens. The supplier shall prepare sketches for purchasers acceptance showing location and sizes of the prolongations or sacrificial forgings and the location of all test specimens within them.

6.4

Test methods

The tensile testing shall be carried out according to ISO 6892. The charpy V-notch impact testing shall be carried out according to ISO 148. The notch shall always be perpendicular to the surface.

6.5

Retesting and criteria for rejection

If one or more of the results fails to meet the requirements, the manufacturer may carry out double set of additional tests, preferably from the same test coupon and position. All results from retest shall meet the requirements. If retesting fails, the forging will be rejected. However the manufacturer may choose to carry out a full reheat treatment (e.g. normalizing + tempering or quenching + tempering) once followed by full set of mechanical testing. If any results still are not acceptable, the forging or lot will be rejected.

NORSOK standard

Page 9 of 13

NORSOK standard M-123

Rev. 2, October 2012

6.6

Mechanical properties
Table 2 Mechanical properties Yield strength Re min MPa Tensile strength Rm min MPa Elongation A5 min % Reduction of area Z min % Impact test KV min J aver./single KV test temp. o C -40 -40 -40 -40 Ratio Re/ Rm max 0,87 0,90 0,90 0,90

Requirements to mechanical properties are given in Table 2.

Steel grade

355 355 470-630 22 50 50/42 420 420 500-660 19 40 50/42 460 460 540-700 17 40 50/42 500 500 600-750 17 40 50/42 For section thicknesses above 250 mm, lower values for Re and Rm may be agreed Re = ReH or Rp0,2

6.7

Summary of mechanical testing

Table 3 Summery of mechanical testing

A summary of mechanical testing is given in Table 3

Test Tensile and impact test

Forging Weight < 1 tonne < 1 tonne > 1 tonne > 1 tonne

Material thickness 50 mm > 50 mm 50 mm > 50 mm

Test frequency To be agreed To be agreed Per forging Per forging

Orientation Transv. and longit. Transv. and longit. Transv. and longit. Transv. and longit.

Test position t/2 t/3 t/2 t/3 + Sub surface

Reference 6.1 and 6.3 6.1 and 6.3 6.1 and 6.3 6.1 and 6.3

7
7.1

Non destructive testing

Personnel

All NDT personnel shall be qualified according to EN 473/Nordtest level II in product sector (c) or an industry sector containing product sector (c) ASNT ACCP level 2 accredited NDT or equivalent. Personnel performing RT exposures only, may, however, be qualified to level I. Personnel qualified to level III, shall be responsible for all NDT activities.ASNT-TC-1A level III personnel shall hold valid ASNT-TC-1A level III Certificate,i.e. management appointed level III is not accepted. Contractor shall keep an updated list of all NDT personnel engaged in the work, with reference to possessed certificates and expiry dates. This list shall be made available to Purchaser on request.

7.2

Critical areas and extent of testing

7.2.1 Critical area Any critical areas shall be identified on design drawings with information about special additional requirements with respect to method and acceptance criteria. All areas shall be subject to NDT as described in 7.2.2.

NORSOK standard

Page 10 of 13

NORSOK standard M-123 7.2.2 Extent of testing Table 4 Extent of non destructive testing Test method Visual examination Magnetic particle testing (MT) Ultrasonic testing (UT)

Rev. 2, October 2012

Extent of testing 100% of accessible surfaces 100% of accessible surfaces 100 % volumetric testing from all accessible surfaces.

Radiographic testing (RT) Note1

100 % of bevel ends within 100 mm from ends and/or critical areas as agreed between the manufacturer and purchaser.

Note: RT of bevel ends and critical areas may be replaced with UT provided UT is carried out in accordance with NORSOK M-101 and the acceptance criteria in 9.8, Table 5, Inspection category A+B.

7.3

Methods

7.3.1 General All NDT shall be carried out in final heat treated condition and in accordance with established procedures. Surface to be inspected shall be clean and free from oil, grease, sand and loose rust or scale that may interfere a satisfactory inspection. 7.3.2 Visual/dimensional examination Methods for visual and/or dimensional examination shall be agreed and specified on approved drawing. 7.3.3 Magnetic particle testing The performance shall be as per ASME V, art.7/ASTM E 709. The surface to be examined shall be machined to a roughness better than N 10 (Ra 12 m), see ISO 2632/III. The tangential field strength shall be min. 25 Oersted and lifting power (AC- Yoke) minimum 45 N at the maximum pole spacing that will be used. 7.3.4 Ultrasonic testing The performance shall be as per ASTM A388 with the following specified details: Surfaces: Machined, better than Ra 12 m see BS 2634-1 for straight beam and better than Ra 6 m for angle beam testing. Probes: 2-4MHz,straight beam and/or angle beam. Straight beam: 10 to24 Angle beam: Preferred probes:20 mm x 22 mm or 8 mm x 9 mm. Probe selection: Straight beam, scanning in two perpendicular directions. If not possible due to difficult configurations: Additional testing with angle probes. Sound attenuation ( permeability): To be checked at different typical locations (cross-sections) of the forging. Any attenuation differences shall be considered during the testing.

NORSOK standard

Page 11 of 13

NORSOK standard M-123

Rev. 2, October 2012

Reference block: Similar to the item inspected related to surface and acoustic response One-block technique: A reference block representing the thickest part of the item tested, containing a flat bottom hole (FBH) 3 mm x15 mm and a side drilled hole (SD) 3 mm x 40 mm at a distance of 1/4 x cross-section. DGS-method: Alternatively, the DGS-method may be used if agreed between the purchaser and manufacturer. Gain reference level: 3mm equivalent reflector. 7.3.5 Radiographic testing The radiographic testing and calibration shall be carried out in accordance with ASME V, Article 2. In addition to procedure, a shooting sketch shall be prepared prior to the testing.

7.4

Acceptance criteria

7.4.1 Visual examination Forgings shall be free of cracks, thermal rupture or other injurious indications. Requirements to surface conditions shall be agreed and specified on approved drawings. 7.4.2 Magnetic particle testing Acceptance criteria shall be in accordance with ASTM A508, section 8.2. 7.4.3 Ultrasonic testing Acceptance criteria for ultrasonic testing are given in table 5 Table 5 Reference level Definition Area 1 High stressed area Core-zone Rim-zone Core-zone Rim-zone Reference level 3 mm equiv. disk reflector 3 mm equiv. disk reflector 6 mm equiv. disk reflector 3 mm equiv. disk reflector

Area 2

Med./low stressed area

Note: If not otherwise agreed: 1) The Rim zone is 0-30 mm from all finished surfaces and Core zone is depths greater than 30 mm from all finished surfaces 2) Weld end zone shall be examined according to Area 1 The evaluation of imperfections shall be at the scanning reference-level related to actual depth. 7.4.4 Radiographic testing The acceptance criteria shall be in accordance with NORSOK M-101, 9.8, Table 6, Inspection category A+B. If radiography is replaced by ultrasonic testing, the acceptance criteria shall be according to 9.8, Table 7, Inspection category A+B.

Repair

Repair by welding is not permitted. Repair by grinding is acceptable. It is a condition that the design wall thickness is maintained. All grinding shall be carried out in accordance with established and accepted procedures. Other kind of repair is not accepted. All repaired areas shall be magnetic particle inspected in accordance with Clause 7. NORSOK standard Page 12 of 13

NORSOK standard M-123

Rev. 2, October 2012

Dimensions/tolerances

Dimensions and required tolerances shall be as given on the relevant drawing of the forgings or other information supplied.

10

Surface protection

All machined surfaces shall be protected by a rust protection coating (tectyl or equivalent).

11

Marking

Forgings shall be marked for identification against a certificate. The marking shall include Contractors identification and heat number. All markings shall be carried out by die stamping and be framed by white painting. The letters used for the stamping should be 15 mm in height.

12

Documentation

Certificate Type 3.1 according to EN 10204 is required. The certificate shall contain all relevant information including, but not restricted to the following: purchasers name and order number; delivery condition; heat number/forging number; description of product, dimension and weight; yield strength, tensile strength, elongation and reduction of area; Charpy V-notch values and test temperature; chemical composition, carbon equivalent/Pcm; visual inspection and NDT, or reference to separate reports;

NORSOK standard

Page 13 of 13